stainless steel sheet 304/304L
stainless steel sheet 304/304L properties and heat treatment forged piece, Including stainless steel sheet 304/304L application and specifications, We have all specifications，Including stainless steel sheet 304/304L steel plate, stainless steel sheet 304/304L sheet, stainless steel sheet 304/304L square steel, stainless steel sheet 304/304L flat bar,stainless steel sheet 304/304L round bar,stainless steel sheet 304/304L forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the stainless steel sheet 304/304L has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade stainless steel sheet 304/304L and Standards
stainless steel Sheets corrosive resistant properties make it ideal for a wide variety of applications.
Detail introduction
Payment & Shipping Terms:
Sheet metal is available as flat pieces or as a coiled strip. The coils are formed by running a continuous sheet of metal through a roll slitter. Type 304 stainless steel sheet has a very low carbon content ( .08 ) With 304L grade material having an even lower amount of carbon content ( .03 ) Less carbon = more corrosion resistance. The thickness of the sheet metal is called its gauge. The gauge of sheet metal ranges from 30 gauge to about 7 gauge. The higher the gauge, the thinner the metal. Thicknesses can vary significantly, although extremely thin thicknesses are considered foil or leaf, and pieces thicker than 6 mm (0.25 in) are considered plate. Standard widths are 36”, 48”, 60” and 72”. Standard lengths are 96” , 120” and 144” with the ability to order longer cut lengths to size at the time the coil is being processed. stainless steel Sheets corrosive resistant properties make it ideal for a wide variety of applications. It is easily welded by most commercial processes with the exception of forging. Ideal applications for stainless sheet include, but not limited to, the processing of food and beverage products as well as, dairy products , beef products and poultry products. Also, high acidity applications such as citric acid and nitric acid are common with stainless sheet products. The food processing industry relies heavily on stainless sheet products for its sanitation properties and ease of cleaning. |
| Browse on aisi 304/304L stainless steel sheet The content |
Machining performance
Download stainless steel sheet 304/304L the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.