AISI 1010
AISI 1010 properties and heat treatment forged piece, Including AISI 1010 application and specifications, We have all specifications，Including AISI 1010 steel plate, AISI 1010 sheet, AISI 1010 square steel, AISI 1010 flat bar,AISI 1010 round bar,AISI 1010 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the AISI 1010 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade AISI 1010 and Standards
| Category | steel |
| Class | Carbon steel |
| Type | Standard |
| Designations | France: AFNOR XC 10 Germany: DIN 1.1121 Japan: JIS S12C , JIS S1OC , JIS S9CK United States: AMS 5040 , AMS 5042 , AMS 5044 , AMS 5047 , AMS 5053 , ASTM A108 , ASTM A29 , ASTM A510 , ASTM A519 , ASTM A545 , ASTM A549 , ASTM A575 , ASTM A576 , MIL SPEC MIL-S-11310 (CS1010) , SAE J403 , SAE J412 , SAE J414 , UNS G10100 |
| Element | Weight % |
| C | 0.08-0.13 |
| Mn | 0.30-0.60 |
| P | 0.04 (max) |
| S | 0.05 (max) |
Properties
Conditions
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
Poisson's Ratio
0.27-0.30
25
Elastic Modulus (GPa)
190-210
25
Tensile Strength (Mpa)
365
25
cold drawn (round bar (19-32 mm)) more
Yield Strength (Mpa)
305
Elongation (%)
20
Reduction in Area (%)
40
Hardness (HB)
105
25
cold drawn (round bar (19-32 mm)) more
Properties
Conditions
T (°C)
Treatment
Thermal Expansion (10-6/ºC)
15
0-700 more
annealed
Thermal Conductivity (W/m-K)
65.2
0 more
Specific Heat (J/kg-K)
450
50-100 more
Machining performance
Download AISI 1010 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.