1.8159
1.8159 properties and heat treatment forged piece, Including 1.8159 application and specifications, We have all specifications，Including 1.8159 steel plate, 1.8159 sheet, 1.8159 square steel, 1.8159 flat bar,1.8159 round bar,1.8159 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the 1.8159 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade 1.8159 and Standards
51CrV4 ( 1.8159 )
Grade :
51CrV4
Number:
1.8159
Standard:
EN 10277 - 5 : 2008 Bright steel products. Technical delivery conditions. steels for quenching and tempering
EN 10083 - 3 : 2006 steels for quenching and tempering. Technical delivery conditions for alloy steels
EN 10132 - 4 : 2000 Cold rolled narrow steel strip for heat treatment. Technical delivery conditions. Spring steels and other applications
Classification:
steels for quenching and tempering
Chemical composition % of the ladle analysis of grade 51CrV4 (1.8159)
C
Si
Mn
P
S
Cr
V
0.47 - 0.55
max 0.4
0.7 - 1.1
max 0.025
max 0.025
0.9 - 1.2
0.1 - 0.25
Technological properties of grade 51CrV4 (1.8159) .
Weldability: ? Bad weldability due to the high crack danger.
Hardenability: ?Good hardenability; suitable for pieces of small sizes and for exacting purposes. It can be hardened in oil.
Equivalent grades of grade 51CrV4 (1.8159)
USA
-Germany
DIN,WNrFrance
AFNOREngland
BSItaly
UNISpain
UNERussia
GOSTInternational
ISO
6150
50CrV4
50CV4
735A50
50CrV4
51CrV4
F1430
50KHGF?
51CrV4
Machining performance
Download 1.8159 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.