1.4541
1.4541 properties and heat treatment forged piece, Including 1.4541 application and specifications, We have all specifications，Including 1.4541 steel plate, 1.4541 sheet, 1.4541 square steel, 1.4541 flat bar,1.4541 round bar,1.4541 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the 1.4541 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade 1.4541 and Standards
X6CrNiTi18-10 ( 1.4541 )
| Grade : | X6CrNiTi18-10 |
| Number: | 1.4541 |
| Standard: | EN 10088 - 2 : 2005 stainless steels. Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes EN 10088 - 3 : 2005 stainless steels. Technical delivery conditions for semi-finished products, bars, rods, wire, sections and bright products of corrosion resisting steels for general purposes |
| Classification: | Austenitic stainless steels - Standard grade |
Chemical composition % of the ladle analysis of grade X6CrNiTi18-10 (1.4541)
| Ti = 5 * C to 0.7 Particular ranges of sulphur content may provide improvement of particular properties. For machinability a controlled sulphur content of 0.015 % to 0.030% is recommended and permitted. For weldability, a controlled sulphur content of 0.008 % to 0.030 % is recommended and permitted. For polishability, a controlled sulphur content of 0.015 % max is recommended. Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast. |
| C | Si | Mn | Ni | P | S | Cr | Ti |
| max 0.08 | max 1 | max 2 | 9 - 12 | max 0.045 | max 0.015 | 17 - 19 | max 0.7 |
Equivalent grades of grade X6CrNiTi18-10 (1.4541)
USA
-Germany
DIN,WNrJapan
JISFrance
AFNOREngland
BSChina
GBSweden
SSPoland
PNFinland
SFSRussia
GOST
321
X10CrNiTi18-9
SUS321
Z6CNT18-10
321S31
0Cr18Ni10Ti
2337
1H18N9T
731
08KH18N10T
08KH18N12T
12KH18N10T
Machining performance
Download 1.4541 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.