X3CRNIMOAL13-8-2, 1.4534, PH13-8MO, UNS S13800
- Smelting Method:
- Delivery status: Forged 、Solutioned 、Ageing 、
- Dimensions: Φ200mm x 500mm
- Surface: Turned 、
- Standard: AMS
Quick Details
Chromium-nickel-molybdenum stainless construction steel with aluminum additive X3CrNiMoAl13-8-2, 1 4534, PH 13-8 Mo, 13-8 Mo precipitation strengthened for use in the aerospace, petroleum and petrochemical industries
Stock Status
Product Details
+A HRC Hardness: <38 HB Hardness: <363 +H950 Tensile strength, Rm: >1515 MPa Yield point, Re: >1415 MPa Elongation, A: >10% HRC Hardness: >45 HB Hardness: >450 +H1000 Tensile strength, Rm: >1415 MPa Yield point, Re: >1310 MPa Elongation, A: >10% HRC Hardness: >43 HB Hardness: >400 +H1025 Tensile strength, Rm: >1280 MPa Yield point, Re: >1210 MPa Elongation, A: >11% HRC Hardness: >41 HB Hardness: >380 +H1050 Tensile strength, Rm: >1210 MPa Yield point, Re: >1140 MPa Elongation, A: >12% HRC Hardness: >40 HB Hardness: >372 +H1100 Tensile strength, Rm: >1035 MPa Yield point, Re: >950 MPa Elongation, A: >14% HRC Hardness: >34 HB Hardness: >313 +H1150 Tensile strength, Rm: >930 MPa Yield point, Re: >620 MPa Elongation, A: >14% HRC Hardness: >30 HB Hardness: >283 +H1150M Tensile strength, Rm: >860 MPa Yield point, Re: >585 MPa Elongation, A: >16% HRC Hardness: >26 HB Hardness: >259
Other signs and equivalents:AMS 5629, ASTM A693 GRADE XM-13, ASTM A564 GRADE XM-13, ASTM A705 GRADE XM-13, PH13-8MO, PH 13-8MO, PH 13-8 MO, N 4534, E 4534, 04CR13NI8MO2AL, X1CRNIMOAL12-9, X 1 CRNIMOAL 12-9, Z4CNDAT13-09, Z 4 CNDAT 13-09, Z1CNDA12-09, Z 1 CNDA 12-09, MARVAL X12, X3CRNIMOAL13-8-2, X 3 CRNIMOAL 13-8-2, 1.4534, N709, 13-8MO, BS13-8, ASTM A959 GRADE XM-13, 13/8MO, X1CRNIMOALTI12-9, AMS 5928, S11800 UNS S13800, XM13, ABS 5442, ABS 5629A/B, AIMS 01-04-002, LN 668 / 1013, LN 1017, AMS 5622, AMS 5643, 1.4530.
+A HRC Hardness: <38 HB Hardness: <363 +H950 Tensile strength, Rm: >1515 MPa Yield point, Re: >1415 MPa Elongation, A: >10% HRC Hardness: >45 HB Hardness: >450 +H1000 Tensile strength, Rm: >1415 MPa Yield point, Re: >1310 MPa Elongation, A: >10% HRC Hardness: >43 HB Hardness: >400 +H1025 Tensile strength, Rm: >1280 MPa Yield point, Re: >1210 MPa Elongation, A: >11% HRC Hardness: >41 HB Hardness: >380 +H1050 Tensile strength, Rm: >1210 MPa Yield point, Re: >1140 MPa Elongation, A: >12% HRC Hardness: >40 HB Hardness: >372 +H1100 Tensile strength, Rm: >1035 MPa Yield point, Re: >950 MPa Elongation, A: >14% HRC Hardness: >34 HB Hardness: >313 +H1150 Tensile strength, Rm: >930 MPa Yield point, Re: >620 MPa Elongation, A: >14% HRC Hardness: >30 HB Hardness: >283 +H1150M Tensile strength, Rm: >860 MPa Yield point, Re: >585 MPa Elongation, A: >16% HRC Hardness: >26 HB Hardness: >259
Other signs and equivalents:AMS 5629, ASTM A693 GRADE XM-13, ASTM A564 GRADE XM-13, ASTM A705 GRADE XM-13, PH13-8MO, PH 13-8MO, PH 13-8 MO, N 4534, E 4534, 04CR13NI8MO2AL, X1CRNIMOAL12-9, X 1 CRNIMOAL 12-9, Z4CNDAT13-09, Z 4 CNDAT 13-09, Z1CNDA12-09, Z 1 CNDA 12-09, MARVAL X12, X3CRNIMOAL13-8-2, X 3 CRNIMOAL 13-8-2, 1.4534, N709, 13-8MO, BS13-8, ASTM A959 GRADE XM-13, 13/8MO, X1CRNIMOALTI12-9, AMS 5928, S11800 UNS S13800, XM13, ABS 5442, ABS 5629A/B, AIMS 01-04-002, LN 668 / 1013, LN 1017, AMS 5622, AMS 5643, 1.4530.