Chemical composition % of the ladle analysis of grade YG6A

Chemical composition (%) | WC: 92
Chemical composition (%) | TiC:-
Chemical composition (%) | TaC (NbC) : 2.0
Chemical composition (%) | Co: 6
Chemical composition (%) | other:-
Density / (g/cm ^ 3) : 14.7 ~ 15.1
Hardness HRA: 91.5
Bending strength σ bb/MPa: 1400
The impact toughness aK / (J/cm ^ 2) :-
Mechanical properties of grade YG6A
Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
568 (≥) 843 (≥) 11 23 42 Solution and Aging, Annealing, Ausaging, Q+T,etc 222
Physical properties of grade YG6A
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
685 (≥) 655 (≥) 44 41 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 434
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
851 395 297
YG6A Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED

Enquiry