X3CrNiM0N27-5-2 Enquiry | Print this page
- Category
- Type
- Steel grade
- Country
- USE
- Grades
- Special Alloy
- » X3CrNiM0N27-5-2
1.4578
1.4563
X1NiCrM0Cu31-27-4
1.4537
X1CrNiM0CuN25-25-5
X1CrNiM0CUN20-18-7
1.4547
1.4529
X1NiCrM0CuN25-20-7
1.4460 - UK
- austenitic special steel
Chemical composition % of the ladle analysis of grade X3CrNiM0N27-5-2
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | N(%) |
| Max 0.050 | Max 1.00 | Max 2.00 | Max 0.035 | Max 0.015① | 25.0-28.0 | 4.50-6.50 | 1.30-2.00 | 0.05-0.20 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 419 (≥) | 912 (≥) | 33 | 42 | 23 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 946 (≥) | 499 (≥) | 21 | 11 | 13 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 133 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 221 | 389 | 312 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |