- » X1CrNiMoNb28-4-2
W-Nr 1.4565
W-Nr 1.4567
X3CrNiCu18-9-4
X7CrNiAI17-7
W-Nr 1.4568
X6CrNiMo17-12-2
W-Nr 1.4571
X10CrNiMoTi18-12
W-Nr 1.4573
W-Nr 1.4573 - DIN
- Germany
- Stainless steel
Chemical composition % of the ladle analysis of grade X1CrNiMoNb28-4-2
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Ni(％) | Mo(％) | N(%) | Nb(%) | Other(%) |
| Max 0.015 | Max 1.00 | Max 1.00 | Max 0.025 | Max 0.015 | 26.0-30.0 | 3.00-4.50 | 1.80-2.50 | Max 0.035 | Max 1.20 | (C+N)Max 0.40 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 534 (≥) | 255 (≥) | 44 | 11 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 322 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 463 (≥) | 781 (≥) | 41 | 41 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 341 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 686 | 555 | 329 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |