UNS G92610
UNS G92610 properties and heat treatment forged piece, Including UNS G92610 application and specifications, We have all specifications，Including UNS G92610 steel plate, UNS G92610 sheet, UNS G92610 square steel, UNS G92610 flat bar,UNS G92610 round bar,UNS G92610 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the UNS G92610 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade UNS G92610 and Standards
AISI 9261 steel (UNS G92610)
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 9000 Series steel; Low Alloy Steel
Key Words: UNS G92610
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.75 g/cc | 0.280 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 514 | 514 | |
| Tensile Strength, Ultimate | 1779 MPa | 258000 psi | |
| Tensile Strength, Yield | 1558 MPa @Strain 0.200 % |
226000 psi @Strain 0.200 % |
|
| Elongation at Break | 10.0 % | 10.0 % | |
| Modulus of Elasticity | 201 - 209 GPa | 29200 - 30300 ksi | |
| Bulk Modulus | 160 - 170 GPa | 23200 - 24700 ksi | |
| Poissons Ratio | 0.270 - 0.300 | 0.270 - 0.300 | |
| Shear Modulus | 81.0 - 82.0 GPa | 11700 - 11900 ksi | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | >= 14.6 µm/m-°C | >= 8.11 µin/in-°F | |
| Specific Heat Capacity | 0.502 J/g-°C @Temperature 50.0 - 100 °C |
0.120 BTU/lb-°F @Temperature 122 - 212 °F |
|
| Thermal Conductivity | >= 46.8 W/m-K | >= 325 BTU-in/hr-ft²-°F | |
Users viewing this material also viewed the following:
AISI 2330 steel (UNS G23300)
AISI 4063 steel (UNS G40630)
Overview of materials for AISI 9000 Series steel
AISI 8750 Steel (UNS G87500)
AISI 9255 Steel, normalized at 900°C (1650°F)
M9261 / 100239
Machining performance
Download UNS G92610 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.