UNS G10100
UNS G10100 properties and heat treatment forged piece, Including UNS G10100 application and specifications, We have all specifications，Including UNS G10100 steel plate, UNS G10100 sheet, UNS G10100 square steel, UNS G10100 flat bar,UNS G10100 round bar,UNS G10100 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the UNS G10100 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade UNS G10100 and Standards
| AISI 1010 steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round or thickness | |
|---|---|
| Categories: | Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon steel |
| Material Notes: | Easily cold formed by heading, extruding, upsetting, bending, and other deforming processes. Uses for wires include electroplated products, such as racks, storage bins, shopping carts, fan guards, and jewelry, and unplated such as wires, staples, hardware, and barbed wire. |
| Key Words: | UNS G10100, AMS 5040, AMS 5042, AMS 5044, AMS 5047, AMS 5053, ASTM A29, ASTM A108, ASTM A510, ASTM A519, ASTM A545, ASTM A549, ASTM A575, ASTM A576, MIL SPEC MIL-S-11310 (CS1010), JIS S 9 CK, SAE J403, SAE J412, SAE J414, DIN 1.1121, AFNOR XC 10 (Fr), JIS S10 C, JIS S 12 C |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Typical for steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 95 | 95 | |
| Hardness, Knoop | 113 | 113 | Converted from Brinell hardness. |
| Hardness, Rockwell B | 55 | 55 | Converted from Brinell hardness. |
| Hardness, Vickers | 98 | 98 | Converted from Brinell hardness. |
| Tensile Strength, Ultimate | 325 MPa | 47100 psi | |
| Tensile Strength, Yield | 180 MPa | 26100 psi | |
| Elongation at Break | 28.0 % | 28.0 % | in 50 mm |
| Reduction of Area | 50.0 % | 50.0 % | |
| Modulus of Elasticity | 200 GPa | 29000 ksi | Typical for steel |
| Bulk Modulus | 140 GPa | 20300 ksi | Typical for steel |
| Poissons Ratio | 0.290 | 0.290 | Typical For Steel |
| Machinability | 55 % | 55 % | Based on AISI 1212 steel. as 100% machinability. The machinability of Group I bar, rod, and wire products can be improved by cold drawing. |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000143 ohm-cm | 0.0000143 ohm-cm | condition unknown |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.2 µm/m-°C @Temperature 0.000 - 100 °C |
6.78 µin/in-°F @Temperature 32.0 - 212 °F |
|
| 13.0 µm/m-°C @Temperature 0.000 - 200 °C |
7.22 µin/in-°F @Temperature 32.0 - 392 °F |
||
| 13.5 µm/m-°C @Temperature 0.000 - 300 °C |
7.50 µin/in-°F @Temperature 32.0 - 572 °F |
||
| 13.8 µm/m-°C @Temperature 0.000 - 400 °C |
7.67 µin/in-°F @Temperature 32.0 - 752 °F |
||
| 14.2 µm/m-°C @Temperature 0.000 - 500 °C |
7.89 µin/in-°F @Temperature 32.0 - 932 °F |
||
| 14.6 µm/m-°C @Temperature 0.000 - 600 °C |
8.11 µin/in-°F @Temperature 32.0 - 1110 °F |
||
| 14.9 µm/m-°C @Temperature 0.000 - 700 °C |
8.28 µin/in-°F @Temperature 32.0 - 1290 °F |
||
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | condition unknown; 50-100°C (122-212°F) |
| 0.498 J/g-°C @Temperature 150 - 200 °C |
0.119 BTU/lb-°F @Temperature 302 - 392 °F |
||
| 0.519 J/g-°C @Temperature 200 - 250 °C |
0.124 BTU/lb-°F @Temperature 392 - 482 °F |
||
| 0.536 J/g-°C @Temperature 250 - 300 °C |
0.128 BTU/lb-°F @Temperature 482 - 572 °F |
||
| 0.565 J/g-°C @Temperature 300 - 350 °C |
0.135 BTU/lb-°F @Temperature 572 - 662 °F |
||
| 0.590 J/g-°C @Temperature 350 - 400 °C |
0.141 BTU/lb-°F @Temperature 662 - 752 °F |
||
| 0.649 J/g-°C @Temperature 400 - 450 °C |
0.155 BTU/lb-°F @Temperature 752 - 842 °F |
||
| 0.729 J/g-°C @Temperature 550 - 600 °C |
0.174 BTU/lb-°F @Temperature 1020 - 1110 °F |
||
| 0.825 J/g-°C @Temperature 650 - 700 °C |
0.197 BTU/lb-°F @Temperature 1200 - 1290 °F |
||
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | Typical steel |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.080 - 0.13 % | 0.080 - 0.13 % | |
| Iron, Fe | 99.18 - 99.62 % | 99.18 - 99.62 % | As remainder |
| Manganese, Mn | 0.30 - 0.60 % | 0.30 - 0.60 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
Users viewing this material also viewed the following:
AISI 1010 Steel, cold drawn
AISI 1010 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round or thickness
AISI 1010 Steel, CQ sheet,1.6-5.8 mm round or thickness
AISI 1008 Steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round
AISI 1008 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round
M1010B / 6783
Machining performance
Download UNS G10100 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.