Tool Steel Specifications
Tool Steel Specifications properties and heat treatment forged piece, Including Tool Steel Specifications application and specifications, We have all specifications，Including Tool Steel Specifications steel plate, Tool Steel Specifications sheet, Tool Steel Specifications square steel, Tool Steel Specifications flat bar,Tool Steel Specifications round bar,Tool Steel Specifications forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the Tool Steel Specifications has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade Tool Steel Specifications and Standards
steel Specifications |
 |
tool steel |  |
|
|
|||
|
Great |
U.S.A |
Germany |
Italy |
Japan |
France |
Spain |
|
B01 |
O1 |
1.2510 |
95MnWCr5KU |
~SKS3 |
90MnWCrV5 90MWCV5 |
F.5220 95MnCrW5 |
|
BD2 |
D2 |
1.2379 X155CrVMo12-1 |
X155CrVMo121KU |
SKD11 |
X160CrMoV12-28 32CDV12-28 |
F.520A |
|
BD3 |
D3 |
1.2080 |
X205Cr12KU |
SKD1 |
X200Cr12 |
F.5212 X210Cr12 |
|
BD6 |
~D6 |
1.2436 |
- |
- |
- |
- |
|
BA2 |
A2 |
1.2363 |
X100CrMoV511KU |
SKD12 |
X100CrMoV5 Z100CDV5 |
F5.227 X100CrMoV5 |
|
BH13 |
H13 |
1.2344 X40CrMoV5-1 |
X40CrMoV511KU |
SKD61 |
X40CrMoV5 |
F.5318 X40CrMoV5 |
|
BS1 |
S1 |
1.2550 |
55WCrV8KU |
- |
55WC20 |
F.5241 |
|
BP20 |
P20 |
1.2311 |
- |
- |
- |
- |
|
- |
420 |
1.2083 |
- |
SUS420J2 |
X40Cr13 |
- |
|
~BP30 |
- |
1.2767 X45NiCrMo4 |
~42NiCrMo157 |
SKH51- |
~Y 35NCD16 |
- |
|
BM2 |
M2 |
1.3343 |
- |
- |
Z85WDCV |
- |
|
BM42 |
M42 |
1.3247 |
HS2-9-1-8 |
SKH59 |
Z110DKCWV |
6-5-2 |
|
BW2 |
W2 |
1.2833 |
- |
- |
105MV01 |
- |
|
BS1407 |
- |
1.2002 |
- |
- |
120C2 |
- |
If the specification you require is not listed, please e-mail us with the full specification and details of your required sizes and quantities.
Machining performance
Download Tool Steel Specifications the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.