JIS SKC11 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » SKC11
SK5M
SK6M
SK7M
SKS2M
SKS5M
SKS7M
SKS51M
SKS81M
SKS95M
SKC3 - JIS
- Japan
- Hollow Steel
Chemical composition % of the ladle analysis of grade SKC11
| C(％) | Si(％) | Mn(％) | Cr(％) | Mo(％) | V(%) |
| 0.85-1.10 | 0.15-0.35 | Max 0.50 | 0.80-1.50 | Max 0.40 | Max 0.25 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 583 (≥) | 166 (≥) | 34 | 11 | 12 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 414 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 998 (≥) | 213 (≥) | 44 | 12 | 11 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 443 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 473 | 474 | 658 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |