DIN S18-1-2-5 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » S18-1-2-5
S6-5-2-5
0.3243
S6-5-2-5S
1.3245
S7-4-2-5
1.3246
S2-10-1-8
1.3247
S2-9-2-8
1.3249 - DIN
- Germany
- High-speed tool steel
Chemical composition % of the ladle analysis of grade S18-1-2-5
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) | V(%) | W(%) | Co(%) |
| 0.75-0.83 | Max 0.45 | Max 0.40 | Max 0.030 | Max 0.030 | 3.80-4.50 | 0.50-0.80 | 1.40-1.70 | 17.5-18.5 | 4.50-5.50 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 779 (≥) | 911 (≥) | 12 | 41 | 41 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 312 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 566 (≥) | 518 (≥) | 24 | 33 | 32 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 442 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 989 | 476 | 589 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |