NITRONIC 60 Stainless Steel
NITRONIC 60 Stainless Steel properties and heat treatment forged piece, Including NITRONIC 60 Stainless Steel application and specifications, We have all specifications，Including NITRONIC 60 Stainless Steel steel plate, NITRONIC 60 Stainless Steel sheet, NITRONIC 60 Stainless Steel square steel, NITRONIC 60 Stainless Steel flat bar,NITRONIC 60 Stainless Steel round bar,NITRONIC 60 Stainless Steel forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the NITRONIC 60 Stainless Steel has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade NITRONIC 60 Stainless Steel and Standards
Nitronic 60 stainless steel provides a significantly lower cost way to fight wear and galling compared with cobalt-bearing and high nickel alloys. Its uniform corrosion resistance is better than Type 304 in most media. Chloride pitting resistance is superior to Type 316. Room temperatrue yield strength is nearly twice that of Types 304 and 316. In addition, Nitronic 60 stainless steel provides excellent high-temperature oxidation resistance and low-temperature impact resistance.
Available Forms
Nitronic 60 stainless steel is available in bar, master alloy pigs, ingots and forging billets. Other forms available include sheet and strip, castings, extrusions, seamless tubing and plate.
Applications Potential
Outstanding galling resistance at both ambient and elevated temperatures makes Nitronic 60 stainless steel a valuable material for valve sterns, seats and trim; fastening systems, including nuts and bolts; screening; chain-drive systems; pins, busings and roller bearings; and pump components such as wear rings and lobes. Nitronic 60 is the most effective wear and galling resistant alloy for bridge pins and other critical construction applications.
Machining performance
Download NITRONIC 60 Stainless Steel the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.