J24054 properties and heat treatment forged piece, Including J24054 application and specifications, We have all specifications，Including J24054 steel plate, J24054 sheet, J24054 square steel, J24054 flat bar,J24054 round bar,J24054 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the J24054 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade J24054 and Standards
MetalTek MTEK J24054 4330 Alloy Steel
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel
Material Notes: Alloys for general structural use.
Applications: Cylinders, rolls, hollow shafts.
Information provided by MetalTek
Cast UNS J24054; Cast Grade 10B; Cast ASTM A487; AMS 5328b; Wrought UNS ; Wrought Grade AISI 4330
| Mechanical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Hardness, Brinell | 285 | 285 | |||
| Tensile Strength, Ultimate | >= 860 MPa | >= 125000 psi | |||
| Tensile Strength, Yield | >= 690 MPa | >= 100000 psi | |||
| Elongation at Break | >= 15.0 % | >= 15.0 % | |||
| Component Elements Properties | Metric | English | Comments | ||
| Carbon, C | 0.20 - 0.30 % | 0.20 - 0.30 % | |||
| Chromium, Cr | 0.40 - 0.60 % | 0.40 - 0.60 % | |||
| Iron, Fe | 95.3 - 98.1 % | 95.3 - 98.1 % | |||
| Manganese, Mn | <= 1.0 % | <= 1.0 % | |||
| Molybdenum, Mo | 0.30 - 0.50 % | 0.30 - 0.50 % | |||
| Nickel, Ni | 1.0 - 1.50 % | 1.0 - 1.50 % | |||
| Silicon, Si | <= 0.80 % | <= 0.80 % | |||
| Descriptive Properties | |||||
| Heat Treatment | Quench & Temper | ||||
Users viewing this material also viewed the following:
Latrobe Lescalloy® 4330+V VAC-ARC High Strength Alloy Steel
Latrobe Lescalloy® 4335+V VAC-ARC High Strength Alloy Steel
AISI 4145 steel
MetalTek MTEK J13345 4130 Alloy Steel
AISI 4340 steel, annealed, 25 mm round
NMETEK117 / 18367
Machining performance
Download J24054 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.