- » E1
M40
K01
K10
K20
K30
V10
V10
V20
V20
V30 - JIS
- Japan
- Drawing Die and top-notch tools carbide
Chemical composition % of the ladle analysis of grade E1
| W(%) | Co(%) |
| 92-96 | 4-8 |
Hardness quartile HRA: 90
Bending strength frequency/MPa:1177
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 257 (≥) | 682 (≥) | 34 | 42 | 42 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 142 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 919 (≥) | 465 (≥) | 31 | 43 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 131 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 636 | 647 | 227 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |
| Grade | Standard | Country | Application |
|---|---|---|---|
| X6CrNiSiNCe19-10 | Welded circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 2: Stainless steel |
||
| 1.4818 | Welded circular steel tubes for mechanical and general engineering purposes - Technical delivery conditions - Part 2: Stainless steel |
||
| GH 3536 | Superalloy GH536 is a kind of added tungsten cobalt and nickel - chromium - molybdenum alloy.GH536 alloy at 1200 ℃ with excellent oxidation resistance at high temperature, also can be applied to the neutral and reducing atmosphere.At the same time GH536 a |
||
| 2.4668 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| NiCr19Fe19Nb5Mo3 | Classification and designation for superalloys and high temperature intermetallic materials |
||
| A 1014 N07718 | Standard Specification for Precipitation-Hardening Bolting (UNS N07718) for High Temperature Service |
||
| B 637 N07718 | Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service |
||
| B 670 N07718 | Precipitation-Hardening Nickel Alloy (UNS N07718) Plate, Sheet, and Strip for High-Temperature Service |
||
| B 983 N07718 | Precipitation Hardened or Cold Worked, Seamless Nickel Alloy Pipe and Tube |
||
| N07718 | Ni-Cr Alloy Precipitation Hardenable |
||
| Inconel 718 | Nickel Alloy, Corrosion and Heat-Resistant, Seamless Tubing 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50Al - 18Fe Consumable Electrode Remelted or Vacuum Induction Melted 1775°F (968°C) Solution Heat Treated |
||
| Inconel 718 | Nickel Alloy, Corrosion and Heat-Resistant, Seamless Tubing 52.5Ni - 19Cr - 3.0Mo - 5.1Cb (Nb) - 0.90Ti - 0.50Al - 18Fe Consumable Electrode Remelted or Vacuum Induction Melted 1775°F (968°C) Solution Heat Treated |