DIN 1.4550
DIN 1.4550 properties and heat treatment forged piece, Including DIN 1.4550 application and specifications, We have all specifications，Including DIN 1.4550 steel plate, DIN 1.4550 sheet, DIN 1.4550 square steel, DIN 1.4550 flat bar,DIN 1.4550 round bar,DIN 1.4550 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the DIN 1.4550 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade DIN 1.4550 and Standards
| Category | steel |
| Class | Stainless steel |
| Type | Austenitic standard |
| Common Names | Chromium-Nickel steel |
| Designations | France: AFNOR Z 6 CNN6 18.10 Germany: DIN 1.4550 Italy: UNI x 8 CrNiNb 18 11 Japan: JIS SUS 347 Sweden: SS 2338 United Kingdom: B.S. 347 S 17 , B.S. ANC 3 Grade B , B.S. En. 58 F , B.S. En. 58 G United States: AMS 5512 , AMS 5556 , AMS 5558 , AMS 5571 , AMS 5575 , AMS 5646 , AMS 5654 , AMS 5674 , AMS 5680 , AMS 5681 , ASME SA182 , ASME SA193 , ASME SA194 , ASME SA213 , ASME SA240 , ASME SA249 , ASME SA312 , ASME SA320 (B8C) , ASME SA358 , ASME SA376 , ASME SA403 , ASME SA409 , ASME SA479 , ASTM A167 , ASTM A182 , ASTM A193 , ASTM A194 , ASTM A213 , ASTM A249 , ASTM A269 , ASTM A271 , ASTM A276 , ASTM A312 , ASTM A314 , ASTM A320 , ASTM A358 , ASTM A376 , ASTM A403 , ASTM A409 , ASTM A430 , ASTM A473 , ASTM A479 , ASTM A493 , ASTM A511 , ASTM A554 , ASTM A580 , ASTM A633 , FED QQ-S-763 , FED QQ-S-766 , FED QQ-W-423 , MIL SPEC MIL-S-23195 , MIL SPEC MIL-S-23196 , MIL SPEC MIL-S-862 , SAE 30347 , SAE J405 (30347) , UNS S34700 |
| Composition |
|
| Mechanical Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Density (×1000 kg/m3) | 8 | 25 | |
| Poisson's Ratio | 0.27-0.30 | 25 | |
| Elastic Modulus (GPa) | 193 | 25 | |
| Tensile Strength (Mpa) | 515 | 25 | hot finished and annealed (plate, sheet, strip) more |
| Yield Strength (Mpa) | 205 | ||
| Elongation (%) | 40 | ||
| Reduction in Area (%) | 50 | ||
| Hardness (HRB) | 88 (max) | 25 | annealed (plate, sheet, strip) |
| Thermal Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Thermal Expansion (10-6/ºC) | 16.6 | 0-100 more | |
| Thermal Conductivity (W/m-K) | 16.1 | 100 more | |
| Specific Heat (J/kg-K) | 500 | 0-100 | |
| Electric Properties |
| Properties | Conditions | ||
| T (°C) | Treatment | ||
| Electric Resistivity (10-9W-m) | 730 | 25 | |
Machining performance
Download DIN 1.4550 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.