Our to produce better steel-based products are the main used in industrial manufacturing various types Spring steelCS95 plate,CS95 Round Bar,CS95 forgings,CS95 suppliers, CS95 Stock,CS95 sheet, CS95 flat bar, CS95 pipe,CS95 tube,CS95 mould,CS95 round ingot,CS95 cold-rolled steel,CS95 coil,CS95 strap steel,CS95 hot-rolled steel,CS95 medium plate, CS95 heavy plate,CS95 shapped bar,CS95 hexahedral bar,CS95,CS95 slab ingot,CS95 slab,CS95 price,CS95 square bar,CS95 square steel,CS95 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of CS95.

Current Location:Home » Products » Spring steel » CS95

Product category

CS95

Data Table for:Products: Spring steel:CS95

CS95 properties and heat treatment forged piece, Including CS95 application and specifications, We have all specifications,Including CS95 steel plate, CS95 sheet, CS95 square steel, CS95 flat bar,CS95 round bar,CS95 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the CS95 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade CS95 and Standards

Both grades are high carbon "spring" steel used in a variety of applications where high tensile strength is required.
CS70 is normally supplied in the annealed condition, in which it is suitable for bending, shaping and forming, before heat treatment. Close International equivalents are Din CK67, AISI/SAE 1070 and Euronorm C67S.
CS80 is usually supplied in the ready hardened or hardened and tempered condition, with a grey, blue or polished finish. The advantage of hardened and tempered steel is that it can be used to produce components that do not require the cost of further hardening.
For Products requiring thinner steel strip or even higher tensile strengths, CS95 is often used, this is equivalent to Euronorm C100S or SAE 1095.
TYPICAL ANALYSIS
CS70 
 
C.
Si.
Mn.
S.
P.
0.70%
0.25%
0.70%
0.015%
0..015%
 
TYPICAL ANALYSIS
CS80
 
C.
Si.
Mn.
S.
P.
0.80%
0.25%
0.70%
0.015%
0.015%
 
TYPICAL ANALYSIS
CS95
 
C.
Si.
Mn.
S.
P.
0.95%
0.25%
0.70%
0.015%
0.015%



Machining performance

Download CS95 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.