Superalloys Alloy L605, HS 25, Alloy L605, R30605, Cobalt Alloy, Corrosion and Heat-Resistant, Welding Wire, 52Co - 20Cr - 10Ni - 15W to AMS 5796

Alloy L605 Superalloys Properties Data

Chemical Composition Description Mechanical Properties Physical Properties Applications Heat Treatment Machinability

Chemical Composition of steel Alloy L605 Superalloys: AMS 5796 ,Cross Reference

Alloy L605 Superalloys Applications and Specifications

Haynes 25™ has an excellent temperature strength and oxidation resistance to 2000 ºF. Haynes 25™ is hot formable between 1900 ºF- 2300 ºF. Also known as Alloy L605, it is better to cold-work Haynes 25™ for bending, spinning and drawing the components.

  • AMS 5796 - Cobalt Alloy, Corrosion and Heat-Resistant, Welding Wire, 52Co - 20Cr - 10Ni - 15W
  • AMS 5759 - Cobalt Alloy, Corrosion and Heat-Resistant, Bars, Forgings, and Rings, 52Co - 20Cr - 10Ni - 15W

Mechanical properties at room temperature for Alloy L605 Superalloys: AMS 5796

Tensile Strength,Rm(MPa)

Yield Strength,Rp 0.2(MPa)

Impact,Kv/Ku(J)

Elongation,A(%)

Reduction of area,(%)

Hardness

Product shapes we supply:

Cross Reference, Equivalent, Similar of Alloy L605 Superalloys grade:

HS 25 Alloy L605 R30605

Conditions & Properties

  • +A Soft annealed
  • +AC Annealed to achieve spheroidization of the carbides
  • +QT Quenched and tempered
  • +WW Warm worked
  • +N Normalized
  • +NT Normalized and tempered
  • +AT Solution annealed
  • +C Cold drawn / Hard
  • +CR Cold rolled
  • +PE Peeled
  • +T Tempered