ASTM A808
ASTM A808 properties and heat treatment forged piece, Including ASTM A808 application and specifications, We have all specifications，Including ASTM A808 steel plate, ASTM A808 sheet, ASTM A808 square steel, ASTM A808 flat bar,ASTM A808 round bar,ASTM A808 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the ASTM A808 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade ASTM A808 and Standards
ASTM A808 Sulfur Restricted >2 to 2-1/2 in. thick, steel plate
Categories: Metal; Ferrous Metal; Alloy Steel; Low Alloy Steel; ASTM steel
Material Notes: High strength, low alloy grade. May be substituted for more expensive normalized grades (A633) in certain applications. Normal uses are applications where notch toughness is an important design consideration.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.85 g/cc | 0.284 lb/in³ | Typical of ASTM steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 123 | 123 | based on conversion from tensile strength |
| Hardness, Rockwell B | 69 | 69 | based on conversion from tensile strength |
| Tensile Strength at Break | >= 414 MPa | >= 60000 psi | |
| Tensile Strength, Yield | >= 290 MPa | >= 42000 psi | |
| Elongation at Break | >= 16.0 % | >= 16.0 % | in 8" |
| >= 20.0 % | >= 20.0 % | in 2", > 24" W | |
| Bend Radius, Minimum | 1.00 t | 1.00 t | ≤3/4" W; ASTM A6 PARA. S14 |
| 1.50 t | 1.50 t | >3/4 to 1" W; ASTM A6 PARA. S14 | |
| 2.00 t | 2.00 t | >1 to 1-1/2" W; ASTM A6 PARA. S14 | |
| 2.50 t | 2.50 t | >1-1/2 to 2" W; ASTM A6 PARA. S14 | |
| 3.00 t | 3.00 t | >2 to 2-1/2" W; ASTM A6 PARA. S14 | |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | <= 0.12 % | <= 0.12 % | |
| Iron, Fe | >= 97.485 % | >= 97.485 % | |
| Manganese, Mn | <= 1.65 % | <= 1.65 % | |
| Niobium, Nb (Columbium, Cb) | 0.020 - 0.10 % | 0.020 - 0.10 % | |
| Phosphorous, P | <= 0.035 % | <= 0.035 % | |
| Silicon, Si | 0.15 - 0.50 % | 0.15 - 0.50 % | |
| Sulfur, S | <= 0.010 % | <= 0.010 % | |
| Vanadium, V | <= 0.10 % | <= 0.10 % | |
Users viewing this material also viewed the following:
Allvac® 718 Nickel Superalloy, Heat Treatment: 982°C (1800°F) + Age
Special Metals INCONEL® Alloy 718
Bethlehem Steel RQC ASTM A678 RQC60 Q&T >1-1/2 to 2-1/2 in. thick, steel plate
Bethlehem Steel ASTM A678 Grade D 3/16 to 3 in. thick, steel plate
Bethlehem Steel ASTM A678 Grade B >1-1/2 to 2-1/2 in. thick, steel plate
NBETH084 / 15443
Machining performance
Download ASTM A808 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.