ASTM A213
ASTM A213 properties and heat treatment forged piece, Including ASTM A213 application and specifications, We have all specifications，Including ASTM A213 steel plate, ASTM A213 sheet, ASTM A213 square steel, ASTM A213 flat bar,ASTM A213 round bar,ASTM A213 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the ASTM A213 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade ASTM A213 and Standards
ASTM A213 T9 9Cr-1Mo steel TUBES FOR BOILERS AND HEAT EXCHANGERS (STBA 26)
Categories: Metal; Ferrous Metal; ASTM Steel; Stainless steel; Cast Stainless Steel; Tool Steel; Cold Work steel
Material Notes: Creep and rupture data provided by NIMS
Key Words: JIS G3462 STBA 26; BS 3059-P2 622-490; ISO 2604 II S38; UNS K90941
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 415 MPa | 60200 psi | |
| Tensile Strength, Yield | 205 MPa | 29700 psi | |
| Elongation at Break | 30.0 % | 30.0 % | |
| Rupture Strength | 25.0 MPa @Temperature 650 °C, Time 100000 hour |
3630 psi @Temperature 1200 °F, Time 100000 hour |
|
| 27.0 - 35.0 MPa @Temperature 625 °C, Time 100000 hour |
3920 - 5080 psi @Temperature 1160 °F, Time 100000 hour |
||
| 39.0 - 46.0 MPa @Temperature 600 °C, Time 100000 hour |
5660 - 6670 psi @Temperature 1110 °F, Time 100000 hour |
||
| 51.0 - 62.0 MPa @Temperature 575 °C, Time 100000 hour |
7400 - 8990 psi @Temperature 1070 °F, Time 100000 hour |
||
| 66.0 - 81.0 MPa @Temperature 550 °C, Time 100000 hour |
9570 - 11700 psi @Temperature 1020 °F, Time 100000 hour |
||
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | <= 0.15 % | <= 0.15 % | |
| Chromium, Cr | 8.0 - 10.0 % | 8.0 - 10.0 % | |
| Iron, Fe | 87.1 - 90.55 % | 87.1 - 90.55 % | |
| Manganese, Mn | 0.30 - 0.60 % | 0.30 - 0.60 % | |
| Molybdenum, Mo | 0.90 - 1.10 % | 0.90 - 1.10 % | |
| Phosphorous, P | <= 0.025 % | <= 0.025 % | |
| Silicon, Si | 0.25 - 1.0 % | 0.25 - 1.0 % | |
| Sulfur, S | <= 0.025 % | <= 0.025 % | |
ASTM A213 T22 2.25Cr-1Mo steel FOR BOILER AND HEAT EXCHANGER SEAMLESS TUBES (STBA 24)
ASTM A213 T5 5Cr-0.5Mo steel TUBES FOR BOILERS AND HEAT EXCHANGERS (STBA 25)
ASTM A213 T2 Alloy Steel, Chromium Molybdenum
ASTM A213 T12 Alloy Steel, Chromium Molybdenum
ASTM A178 C 0.2C SILICON-KILLED STEEL TUBES FOR BOILERS AND HEAT EXCHANGERS (STB 410)
NIMS017 / 77534
Machining performance
Download ASTM A213 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.