AISI Type S1
AISI Type S1 properties and heat treatment forged piece, Including AISI Type S1 application and specifications, We have all specifications，Including AISI Type S1 steel plate, AISI Type S1 sheet, AISI Type S1 square steel, AISI Type S1 flat bar,AISI Type S1 round bar,AISI Type S1 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the AISI Type S1 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade AISI Type S1 and Standards
Categories: Metal; Ferrous Metal; Alloy steel; Medium Alloy Steel; tool steel; Shock-Resisting steel
Material Notes: Chromium-tungsten tool steel that provides excellent service in both hot and cold work shock applications. Has good wear resistance and high hardness value.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.83 g/cc | 0.283 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Knoop | 682 | 682 | Converted from Rockwell C Hardness. |
| Hardness, Rockwell C | 58 | 58 | |
| Hardness, Vickers | 661 | 661 | Converted from Rockwell C Hardness. |
| Tensile Strength, Ultimate | 2310 MPa | 335000 psi | |
| Tensile Strength, Yield | 1750 MPa | 254000 psi | |
| Elongation at Break | 9.00 % | 9.00 % | |
| Bulk Modulus | 140 GPa | 20300 ksi | Typical for steel |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 12.4 µm/m-°C | 6.89 µin/in-°F | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 205 - 650 °C | 401 - 1200 °F | Tempering Temperature |
| 900 - 955 °C | 1650 - 1750 °F | Hardening Temperature | |
| Annealing Temperature | 790 - 815 °C | 1450 - 1500 °F | |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.40 - 0.55 % | 0.40 - 0.55 % | |
| Chromium, Cr | 1.40 % | 1.40 % | |
| Iron, Fe | 94.0 % | 94.0 % | |
| Manganese, Mn | 0.25 % | 0.25 % | |
| Molybdenum, Mo | <= 0.50 % | <= 0.50 % | |
| Phosphorous, P | <= 0.030 % | <= 0.030 % | |
| Silicon, Si | 0.680 % | 0.680 % | |
| Sulfur, S | <= 0.030 % | <= 0.030 % | |
| Tungsten, W | 2.25 % | 2.25 % | |
| Vanadium, V | 0.230 % | 0.230 % | |
Users viewing this material also viewed the following:
AISI Type S1 tool steel, quenched 955°C (1750°F), tempered 250°C (500°F)
AISI Type S2 tool steel, austenitized 845°C (1550°F), brine quenched to 55 HRC
AISI Type S5 tool steel, austenitized 855-870°C (1575-1600°F), oil quenched to 55 HRC
AISI Type A2 tool steel
Overview of materials for Medium Alloy Steel
MSS1A / 14086
Machining performance
Download AISI Type S1 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.