AISI 4820
AISI 4820 properties and heat treatment forged piece, Including AISI 4820 application and specifications, We have all specifications，Including AISI 4820 steel plate, AISI 4820 sheet, AISI 4820 square steel, AISI 4820 flat bar,AISI 4820 round bar,AISI 4820 forgings, we can own production and sales.
Introduction to Our Products:
Specialized high quality steel
We have the advantages of equipment, technologies and price
forged/hot rolling/ extrusion of steel
We can produce the AISI 4820 has the following specifications:
Round bar steel: 1mm to 3000mm
Square-shape steel: 1mm to 2000mm
Plate steel:0.1mm to 2500mm
Width: 10mm to 2500mm
Lenth: We can supply any lenth based on the customer's requirement.
Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes
Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.
Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement
Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement
Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.
Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.
We serve you with our honesty, integrity, and professionality.
Chemical composition % of the ladle analysis of grade AISI 4820 and Standards
AISI 4820 steel, heat treated, machined to 13.7 mm, pseudocarburized, 150°C (300°F) temper
Categories: Metal; Ferrous Metal; Alloy Steel; AISI 4000 Series steel; Low Alloy Steel; Carbon Steel; Low Carbon steel
Material Notes: Normalized 925°C (1700°F) in 32mm rounds, machined to 13.7 mm rounds, pseudocarburized at 925°C (1700°F) for 8 h., oil quenched, 150°C (300°F) temper, machined and tested in 12.8mm rounds.
Key Words: SAE 770, low carbon steels, UNS G48200, ASTM A322, ASTM A331, ASTM A505, ASTM A519, ASTM A535, SAE J404, SAE J414,
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.85 g/cc | 0.284 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 415 | 415 | |
| Hardness, Knoop | 446 | 446 | Converted from Brinell hardness. |
| Hardness, Rockwell B | 103 | 103 | Converted from Brinell hardness. |
| Hardness, Rockwell C | 45 | 45 | Converted from Brinell hardness. |
| Hardness, Vickers | 440 | 440 | Converted from Brinell hardness. |
| Tensile Strength, Ultimate | 1448 MPa | 210000 psi | |
| Tensile Strength, Yield | 1138 MPa @Strain 0.200 % |
165100 psi @Strain 0.200 % |
|
| Elongation at Break | 12.3 % | 12.3 % | in 50 mm. |
| Modulus of Elasticity | 205 GPa | 29700 ksi | Typical for steel |
| Bulk Modulus | 140 GPa | 20300 ksi | Typical for steel |
| Poissons Ratio | 0.290 | 0.290 | Calculated |
| Machinability | 50 % | 50 % | annealed and cold drawn. Based on 100% machinability for AISI 1212 steel. |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000245 ohm-cm | 0.0000245 ohm-cm | Typical 4000 series steel |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 0.475 J/g-°C | 0.114 BTU/lb-°F | Typical 4000 series steel |
| Thermal Conductivity | 44.5 W/m-K | 309 BTU-in/hr-ft²-°F | Typical steel |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.180 - 0.230 % | 0.180 - 0.230 % | |
| Iron, Fe | 94.645 - 95.72 % | 94.645 - 95.72 % | As remainder |
| Manganese, Mn | 0.500 - 0.700 % | 0.500 - 0.700 % | |
| Molybdenum, Mo | 0.200 - 0.300 % | 0.200 - 0.300 % | |
| Nickel, Ni | 3.25 - 3.75 % | 3.25 - 3.75 % | |
| Phosphorous, P | <= 0.0350 % | <= 0.0350 % | |
| Silicon, Si | 0.150 - 0.300 % | 0.150 - 0.300 % | |
| Sulfur, S | <= 0.0400 % | <= 0.0400 % | |
Users viewing this material also viewed the following:
AISI 4820 Steel, double quenched and tempered (150°C (300°F)), 1.2 mm case depth
AISI 4820 Steel, direct quenched from pot, tempered (230°C (450°F)), 0.99 mm case depth
AISI 4820 Steel, normalized 860°C (1580°F), 100 mm (4 in.) round
AISI 4820 Steel, mock carburized, reheated to 800°C (1470°F), 150°C (300°F) temper, 13 mm (0.5 in.) round
AISI 4820 Steel, normalized 860°C (1580°F)
M482AP / 7985
Machining performance
Download AISI 4820 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>
Principal Design Features
One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.
Machinability
Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.
Heat Treatment
CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.
Welding
Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.
Forging
Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.