- » 65MnCrMo4
1.2842
90MnCrV8
1.2880
X165CrCoMo12
1.2884
X210CrCoW12
1.2082
X21Cr13
59CrV4
38SiCrV6 - DIN
- Germany
- Hot working alloy tool steel
Chemical composition % of the ladle analysis of grade 65MnCrMo4
| C(％) | Si(％) | Mn(％) | P(％) | S(％) | Cr(％) | Mo(％) |
| 0.60-0.68 | 0.30-0.50 | 1.00-1.20 | Max 0.035 | Max 0.035 | 0.60-0.80 | 0.20-0.30 |
| Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
|---|---|---|---|---|---|---|
| 396 (≥) | 372 (≥) | 11 | 12 | 14 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 143 |
| Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
|---|---|---|---|---|---|---|---|
| 438 (≥) | 844 (≥) | 21 | 31 | 33 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 123 | |
| Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
| 445 | 584 | 141 |
| Product type | Products | Dimension | Processes | Deliver Status |
|---|---|---|---|---|
| Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
| Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
| Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |