Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless Steel65MN plate,65MN Round Bar,65MN forgings,65MN suppliers, 65MN Stock,65MN sheet, 65MN flat bar, 65MN pipe,65MN tube,65MN mould,65MN round ingot,65MN cold-rolled steel,65MN coil,65MN strap steel,65MN hot-rolled steel,65MN medium plate, 65MN heavy plate,65MN shapped bar,65MN hexahedral bar,65MN,65MN slab ingot,65MN slab,65MN price,65MN square bar,65MN square steel,65MN wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of 65MN.

Current Location:Home » Products » Stainless Steel » 65MN

Product category

65MN

Data Table for:Products: Stainless Steel:65MN

65MN properties and heat treatment forged piece, Including 65MN application and specifications, We have all specifications,Including 65MN steel plate, 65MN sheet, 65MN square steel, 65MN flat bar,65MN round bar,65MN forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the 65MN has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade 65MN and Standards

professional manufacturer of 50#, 40Mn, 65Mn, 60Si2Mn, SK4, SK5, SK7, and special steel strips and high-precision stainless steel spring leaves. We are well equipped with strong technical power, and advanced equipments such as continuum acid cleaning lines, six-roller reversible cold rolling units for hydraulic PC control system, bell type bright annealing furnaces, precision splitting machines, temper mills, edge trimmers, and exquisite techniques. Our productivity is very strong. All finished goods have a straight surface, an average tolerance of thickness, a clean surface, and quality up to national standards. We can make products of thickness and width required by the customer. We can make various spring steel leaves, shoe iron, hair grips, writing cases, electronic products, high temperature-resistant elements, punching hardware pieces. We also can produce high-strength thermal treatment strip steel and band saws of all specifications. What's more, we sell 45#, 65#, 70#, 65Mn, T9A, T8MnA, 60SiMn2, 50CrV spring steel wires whose diameters range from o.1 to 10.0 mm.




Machining performance

Download 65MN the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:65MN steel plate, 65MN sheet, 65MN square steel, 65MN flat bar,65MN round bar,65MN forgings