DIN 30WCrV15-1 Enquiry | Print this page
- Category
- Type
- Steel grade
- Standard
- Country
- USE
- Grades
- Special Alloy
- » 30WCrV15-1
X50CrMoV5-1
1.2345
50CrMoV13-14
1.2357
X48CrMoV8-1-1
1.2360
X32CrMoV3-3
1.2365
X38CrMoV5-3
1.2367 - DIN
- Germany
- Hot working alloy tool steel
Chemical composition % of the ladle analysis of grade 30WCrV15-1
C(%) | Si(%) | Mn(%) | P(%) | S(%) | Cr(%) | V(%) | W(%) |
0.25-0.35 | 0.80-1.10 | 0.30-0.50 | Max 0.035 | Max 0.035 | 0.90-1.20 | 0.15-0.20 | 3.50-4.00 |
Proof strength Rp0.2 (MPa) |
Tensile strength Rm (MPa) |
Impact energy KV (J) |
Elongation at fracture A (%) |
Reduction in cross section on fracture Z (%) |
As-Heat-Treated Condition | Brinell hardness (HBW) |
---|---|---|---|---|---|---|
921 (≥) | 553 (≥) | 14 | 12 | 21 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 223 |
Property | Density kg/dm3 |
Temperature T °C/F |
Specific heat J / kgK |
Thermal conductivity W/mK |
Electric resistance µΩ·cm |
Modulus of elasticity kN/mm2 |
Expansion rate |
---|---|---|---|---|---|---|---|
489 (≥) | 141 (≥) | 41 | 22 | 24 | Solution and Aging, Annealing, Ausaging, Q+T,etc | 314 | |
Temp. °C/°F |
Creep strain limit (10000h) (Rp1,0) N/mm2 |
Creep rupture strength (10000h) (Rp1,0) N/mm2 |
|||||
356 | 161 | 293 |
Product type | Products | Dimension | Processes | Deliver Status |
---|---|---|---|---|
Plates / Sheets | Plates / Sheets | 0.08-200mm(T)*W*L | Forging, hot rolling and cold rolling | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Steel Bar | Round Bar, Flat Bar, Square Bar | Φ8-1200mm*L | Forging, hot rolling and cold rolling, Cast | Black, Rough Turning, Shot Blasting, |
Coil / Strip | Steel Coil /Steel Strip | 0.03-16.0x1200mm | Cold-Rolled & Hot-Rolled | Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting |
Pipes / Tubes | Seamless Pipes/Tubes, Welded Pipes/Tubes | OD:6-219mm x WT:0.5-20.0mm | Hot extrusion, Cold Drawn, Welded | Annealed, Solution and Aging, Q+T, ACID-WASHED |