21CMoV5-7,1.7709,21CRMOV5-11,1.8070 Forgings
- Smelting Method:
- Delivery status: Forged 、Q+T 、
- Dimensions: Dia.605mm x 120mm
- Surface: Turned 、
- Standard: DIN
Quick Details
Tensile strength, Rm = 700 - 850 MPa Yield point, Re > 550 MPa Elongation, A > 16% Contraction, Z > 60% Notch toughness, KV20℃ > 63 J
Stock Status
Product Details
mechanical properties of 21CMoV5-7,1.7709 QT
- Tensile strength, Rm = 700 - 850 MPa
- Yield point, Re > 550 MPa
- Elongation, A > 16% Contraction,
- Z > 60% Notch toughness, KV20℃ > 63 J
Softening at 650 °C with slow cooling Slow relief annealing at 530 °C at furnace to at least 200 Normalizing at 950 - 980℃ with cooling in calm air Hardening at 930 - 950℃ in water, 940 - 960℃ in oil Tempering at a temperature of 650 ° c in the air for many hours depending on the size of the material
mechanical properties of 21CMoV5-7,1.7709 QT
- Tensile strength, Rm = 700 - 850 MPa
- Yield point, Re > 550 MPa
- Elongation, A > 16% Contraction,
- Z > 60% Notch toughness, KV20℃ > 63 J
Softening at 650 °C with slow cooling Slow relief annealing at 530 °C at furnace to at least 200 Normalizing at 950 - 980℃ with cooling in calm air Hardening at 930 - 950℃ in water, 940 - 960℃ in oil Tempering at a temperature of 650 ° c in the air for many hours depending on the size of the material