Chemical composition % of the ladle analysis of grade 08X18H10T

C(％) Si(％) Mn(％) P(％) S(％) Cr(％) Ni(％) Mo(％) W(%) Ti(%)
Max 0.08 Max 0.80 Max 2.00 Max 0.035 Max 0.02 17.0-19.0 9.0-11.0 Max 0.30 Max 0.20 5xC-0.70
08X18H10T
Mechanical properties of grade 08X18H10T
Proof strength
Rp0.2 (MPa)		 Tensile strength
Rm (MPa)		 Impact energy
KV (J)		 Elongation at fracture
A (%)		 Reduction in cross section on fracture
Z (%)		 As-Heat-Treated Condition Brinell hardness (HBW)
866 (≥) 683 (≥) 21 41 43 Solution and Aging, Annealing, Ausaging, Q+T,etc 243
Physical properties of grade 08X18H10T
Property Density
kg/dm3		 Temperature T
°C/F		 Specific heat
J / kgK		 Thermal conductivity
W/mK		 Electric resistance
µΩ·cm		 Modulus of elasticity
kN/mm2		 Expansion rate
684 (≥) 191 (≥) 11 42 11 Solution and Aging, Annealing, Ausaging, Q+T,etc 331
Temp.
°C/°F		 Creep strain limit
(10000h)
(Rp1,0) N/mm2		 Creep rupture strength
(10000h)
(Rp1,0) N/mm2
877 797 764
08X18H10T Range of products
Product type Products Dimension Processes Deliver Status
Plates / Sheets Plates / Sheets 0.08-200mm(T)*W*L Forging, hot rolling and cold rolling Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Steel Bar Round Bar, Flat Bar, Square Bar Φ8-1200mm*L Forging, hot rolling and cold rolling, Cast Black, Rough Turning, Shot Blasting,
Coil / Strip Steel Coil /Steel Strip 0.03-16.0x1200mm Cold-Rolled & Hot-Rolled Annealed, Solution and Aging, Q+T, ACID-WASHED, Shot Blasting
Pipes / Tubes Seamless Pipes/Tubes, Welded Pipes/Tubes OD:6-219mm x WT:0.5-20.0mm Hot extrusion, Cold Drawn, Welded Annealed, Solution and Aging, Q+T, ACID-WASHED
Cross Reference Table(Equivalent Grade)
Grade Standard Country Application
08X18H10T
Russia GOCT standard stainless steel and heat resistant steel steel grade and chemical composition

Enquiry