Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelZ6CA13 plate,Z6CA13 Round Bar,Z6CA13 forgings,Z6CA13 suppliers, Z6CA13 Stock,Z6CA13 sheet, Z6CA13 flat bar, Z6CA13 pipe,Z6CA13 tube,Z6CA13 mould,Z6CA13 round ingot,Z6CA13 cold-rolled steel,Z6CA13 coil,Z6CA13 strap steel,Z6CA13 hot-rolled steel,Z6CA13 medium plate, Z6CA13 heavy plate,Z6CA13 shapped bar,Z6CA13 hexahedral bar,Z6CA13,Z6CA13 slab ingot,Z6CA13 slab,Z6CA13 price,Z6CA13 square bar,Z6CA13 square steel,Z6CA13 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Z6CA13.

Current Location:Home » Products » Stainless Steel » Z6CA13

Product category

Z6CA13

Data Table for:Products: Stainless Steel:Z6CA13

Z6CA13 properties and heat treatment forged piece, Including Z6CA13 application and specifications, We have all specifications,Including Z6CA13 steel plate, Z6CA13 sheet, Z6CA13 square steel, Z6CA13 flat bar,Z6CA13 round bar,Z6CA13 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Z6CA13 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Z6CA13 and Standards

Step Shaft Z6CA13 Tube Z6CA13 Pie-shaped Z6CA13 Ring Z6CA13 Module Z6CA13 Large valves of the main Z6CA13 Other Profiled Forgings Z6CA13

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.




Machining performance

Download Z6CA13 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.