Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelY1Cr18Ni9 plate,Y1Cr18Ni9 Round Bar,Y1Cr18Ni9 forgings,Y1Cr18Ni9 suppliers, Y1Cr18Ni9 Stock,Y1Cr18Ni9 sheet, Y1Cr18Ni9 flat bar, Y1Cr18Ni9 pipe,Y1Cr18Ni9 tube,Y1Cr18Ni9 mould,Y1Cr18Ni9 round ingot,Y1Cr18Ni9 cold-rolled steel,Y1Cr18Ni9 coil,Y1Cr18Ni9 strap steel,Y1Cr18Ni9 hot-rolled steel,Y1Cr18Ni9 medium plate, Y1Cr18Ni9 heavy plate,Y1Cr18Ni9 shapped bar,Y1Cr18Ni9 hexahedral bar,Y1Cr18Ni9,Y1Cr18Ni9 slab ingot,Y1Cr18Ni9 slab,Y1Cr18Ni9 price,Y1Cr18Ni9 square bar,Y1Cr18Ni9 square steel,Y1Cr18Ni9 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Y1Cr18Ni9.

Current Location:Home » Products » Tool steel » Y1Cr18Ni9

Product category

Y1Cr18Ni9

Data Table for:Products: Tool steel:Y1Cr18Ni9

Y1Cr18Ni9 properties and heat treatment forged piece, Including Y1Cr18Ni9 application and specifications, We have all specifications,Including Y1Cr18Ni9 steel plate, Y1Cr18Ni9 sheet, Y1Cr18Ni9 square steel, Y1Cr18Ni9 flat bar,Y1Cr18Ni9 round bar,Y1Cr18Ni9 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Y1Cr18Ni9 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Y1Cr18Ni9 and Standards

Step Shaft Y1Cr18Ni9 Tube Y1Cr18Ni9 Pie-shaped Y1Cr18Ni9 Ring Y1Cr18Ni9 Module Y1Cr18Ni9 Large valves of the main Y1Cr18Ni9 Other Profiled Forgings Y1Cr18Ni9

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

Forging/hot rolling/ extrusion of steel

Specifications

Round bar steel: 1mm to 2000mm

Square-shape steel: 50mm  to  600mm

Plate steel:0.1mm  to  800mm

Width: 10mm to 1500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot Forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirement

Excellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.




Machining performance

Download Y1Cr18Ni9 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Y1Cr18Ni9 steel plate, Y1Cr18Ni9 sheet, Y1Cr18Ni9 square steel, Y1Cr18Ni9 flat bar,Y1Cr18Ni9 round bar,Y1Cr18Ni9 forgings