Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelX20CrMo13 plate,X20CrMo13 Round Bar,X20CrMo13 forgings,X20CrMo13 suppliers, X20CrMo13 Stock,X20CrMo13 sheet, X20CrMo13 flat bar, X20CrMo13 pipe,X20CrMo13 tube,X20CrMo13 mould,X20CrMo13 round ingot,X20CrMo13 cold-rolled steel,X20CrMo13 coil,X20CrMo13 strap steel,X20CrMo13 hot-rolled steel,X20CrMo13 medium plate, X20CrMo13 heavy plate,X20CrMo13 shapped bar,X20CrMo13 hexahedral bar,X20CrMo13,X20CrMo13 slab ingot,X20CrMo13 slab,X20CrMo13 price,X20CrMo13 square bar,X20CrMo13 square steel,X20CrMo13 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of X20CrMo13.

Current Location:Home » Products » Stainless Steel » X20CrMo13

Product category

X20CrMo13

Data Table for:Products: Stainless Steel:X20CrMo13

X20CrMo13 properties and heat treatment forged piece, Including X20CrMo13 application and specifications, We have all specifications,Including X20CrMo13 steel plate, X20CrMo13 sheet, X20CrMo13 square steel, X20CrMo13 flat bar,X20CrMo13 round bar,X20CrMo13 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the X20CrMo13 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade X20CrMo13 and Standards

Composition in % :

C
Si
Mn
P
S
Cr
Mo
Ni
0,17 - 0,22
max. 1,00
max. 1,00
max. 0,040
max. 0,015
12,00 - 14,00
0,90 - 1,30
max. 1,00

V
W
Ti
Cu
Al
Nb
B
N
 
 
 
 
 
 
 
 


Range of application and heat treatment :

Stainless steel / Tool steel for hot working : turbine blades , valve cones , moulding plates 
Hardening : 980 - 1030 °C (oil or air)          Soft annealing : 760 - 780 °C 

General and distinctive features :



Machining performance

Download X20CrMo13 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.