Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelX1CrNb15 plate,X1CrNb15 Round Bar,X1CrNb15 forgings,X1CrNb15 suppliers, X1CrNb15 Stock,X1CrNb15 sheet, X1CrNb15 flat bar, X1CrNb15 pipe,X1CrNb15 tube,X1CrNb15 mould,X1CrNb15 round ingot,X1CrNb15 cold-rolled steel,X1CrNb15 coil,X1CrNb15 strap steel,X1CrNb15 hot-rolled steel,X1CrNb15 medium plate, X1CrNb15 heavy plate,X1CrNb15 shapped bar,X1CrNb15 hexahedral bar,X1CrNb15,X1CrNb15 slab ingot,X1CrNb15 slab,X1CrNb15 price,X1CrNb15 square bar,X1CrNb15 square steel,X1CrNb15 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of X1CrNb15.

Current Location:Home » Products » Stainless Steel » X1CrNb15

Product category

X1CrNb15

Data Table for:Products: Stainless Steel:X1CrNb15

X1CrNb15 properties and heat treatment forged piece, Including X1CrNb15 application and specifications, We have all specifications,Including X1CrNb15 steel plate, X1CrNb15 sheet, X1CrNb15 square steel, X1CrNb15 flat bar,X1CrNb15 round bar,X1CrNb15 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the X1CrNb15 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade X1CrNb15 and Standards

X1CrNb15 ( 1.4595 )

  Grade :     X1CrNb15
    Number:     1.4595
    Standard: EN 10088 - 2 : 2005   stainless steels. Technical delivery conditions for sheet/plate and strip of corrosion resisting steels for general purposes
    Classification:     Ferritic stainless steels - special grade

Chemical composition % of the ladle analysis   of grade   X1CrNb15 (1.4595)

Elements not listed in this table shall not be intentionally added to the steel without the agreement of the purchaser except for finishing the cast.
 

C Si Mn P S Cr N Nb
max   0.02 max   1 max   1 max   0.025 max   0.015 14 - 16 max   0.02 0.2 - 0.6




Machining performance

Download X1CrNb15 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.