Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelUNS S32760 plate,UNS S32760 Round Bar,UNS S32760 forgings,UNS S32760 suppliers, UNS S32760 Stock,UNS S32760 sheet, UNS S32760 flat bar, UNS S32760 pipe,UNS S32760 tube,UNS S32760 mould,UNS S32760 round ingot,UNS S32760 cold-rolled steel,UNS S32760 coil,UNS S32760 strap steel,UNS S32760 hot-rolled steel,UNS S32760 medium plate, UNS S32760 heavy plate,UNS S32760 shapped bar,UNS S32760 hexahedral bar,UNS S32760,UNS S32760 slab ingot,UNS S32760 slab,UNS S32760 price,UNS S32760 square bar,UNS S32760 square steel,UNS S32760 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of UNS S32760.

Current Location:Home » Products » Stainless Steel » UNS S32760

Product category

UNS S32760

Data Table for:Products: Stainless Steel:UNS S32760

UNS S32760 properties and heat treatment forged piece, Including UNS S32760 application and specifications, We have all specifications,Including UNS S32760 steel plate, UNS S32760 sheet, UNS S32760 square steel, UNS S32760 flat bar,UNS S32760 round bar,UNS S32760 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the UNS S32760 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade UNS S32760 and Standards

UNS S32760, F55, 1.4501 Super Duplex has enhanced pitting and crevice corrosion resistance compared with the ordinary austenitic or duplex types. This is due to the further additions of chromium, molybdenum, and nitrogen to these grades. UNS S32760, F55, 1.4501 combines high strength and good ductility with outstanding corrosion resistance. With UNS S32760, F55, 1.4501 having these attribute it is used in a wide range of marine, oil and gas environments. UNS S32760, F55, 1.4501 is the most common super duplex grade.
    

TYPICAL ANALYSIS                
 C. Cr. Cu. Mn. Mo. N. Ni. P. S. Si. W.
0.03% 24.00- 0.50- 1.00% 3.00- 0.20- 6.00- 0.035% 0.015% 1.00% 0.50-
max 26.00% 1.00% max 4.00% 0.30% 8.00% max max max 1.00%
 
 
 
Minimum Mechanical Properties at Room Temperature
(EN10088-3 1.4501 UNS S32760 F55 160mm dia max - solution treated)

 Tensile (UTS)

 
730 - 930 N/mm²
 0.2% Proof Stress
 
530 N/mm² Min
 Elongation 
 
25% min
 Hardness
 
290HB Max
 Impact
 
100J

 

 
 
 Super Duplex Stainless Steel Specifications  EN10088-3 UNS S32760 F55 1.4501 Grade X2CrNiMoCuWN25-7-4  ASTM A182 F55 NACE MR01-75 ISI 15156ASTM A276 A314 SAE J405 Norsok MDS D51 D55 D57 D58



Machining performance

Download UNS S32760 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:UNS S32760 steel plate, UNS S32760 sheet, UNS S32760 square steel, UNS S32760 flat bar,UNS S32760 round bar,UNS S32760 forgings