Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi-2.5Cu plate,Ti-2.5Cu Round Bar,Ti-2.5Cu forgings,Ti-2.5Cu suppliers, Ti-2.5Cu Stock,Ti-2.5Cu sheet, Ti-2.5Cu flat bar, Ti-2.5Cu pipe,Ti-2.5Cu tube,Ti-2.5Cu mould,Ti-2.5Cu round ingot,Ti-2.5Cu cold-rolled steel,Ti-2.5Cu coil,Ti-2.5Cu strap steel,Ti-2.5Cu hot-rolled steel,Ti-2.5Cu medium plate, Ti-2.5Cu heavy plate,Ti-2.5Cu shapped bar,Ti-2.5Cu hexahedral bar,Ti-2.5Cu,Ti-2.5Cu slab ingot,Ti-2.5Cu slab,Ti-2.5Cu price,Ti-2.5Cu square bar,Ti-2.5Cu square steel,Ti-2.5Cu wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti-2.5Cu.

Current Location:Home » Products » Ti Alloy » Ti-2.5Cu

Product category

Ti-2.5Cu

Data Table for:Products: Ti Alloy:Ti-2.5Cu

Ti-2.5Cu properties and heat treatment forged piece, Including Ti-2.5Cu application and specifications, We have all specifications,Including Ti-2.5Cu steel plate, Ti-2.5Cu sheet, Ti-2.5Cu square steel, Ti-2.5Cu flat bar,Ti-2.5Cu round bar,Ti-2.5Cu forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti-2.5Cu has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti-2.5Cu and Standards

Titanium IMI 230 (Ti-2.5Cu)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Near Alpha Titanium Alloy

Material Notes: Annealed; Aging increases Strength

Physical Properties Metric English Comments
Density  4.56 g/cc 0.165 lb/in³
 
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate  620 MPa 89900 psi
Tensile Strength, Yield  480 MPa 69600 psi
Elongation at Break  24.0 % 24.0 %
Modulus of Elasticity  105 GPa 15200 ksi
Poissons Ratio  0.310 0.310 Typical for alpha titanium alloy.
Fatigue Strength  280 MPa
@# of Cycles 1.00e+7
40600 psi
@# of Cycles 1.00e+7
Shear Modulus  40.1 GPa 5820 ksi Calculated from typical values.
 
Electrical Properties Metric English Comments
Electrical Resistivity  0.0000650 ohm-cm 0.0000650 ohm-cm
 
Thermal Properties Metric English Comments
CTE, linear 9.02 µm/m-°C
@Temperature 20.0 - 100 °C
5.01 µin/in-°F
@Temperature 68.0 - 212 °F
  9.10 µm/m-°C
@Temperature 20.0 - 300 °C
5.06 µin/in-°F
@Temperature 68.0 - 572 °F
average
  9.46 µm/m-°C
@Temperature 20.0 - 600 °C
5.26 µin/in-°F
@Temperature 68.0 - 1110 °F
average
Specific Heat Capacity  0.525 J/g-°C 0.125 BTU/lb-°F Typical value for titanium alloys.
Thermal Conductivity  13.0 W/m-K 90.2 BTU-in/hr-ft²-°F
Beta Transus  895 °C 1640 °F
 
Component Elements Properties Metric English Comments
Carbon, C  <= 0.0800 % <= 0.0800 %
Copper, Cu  2.00 - 3.00 % 2.00 - 3.00 %
Hydrogen, H  <= 0.0100 % <= 0.0100 %
Iron, Fe  <= 0.200 % <= 0.200 %
Nitrogen, N  <= 0.0500 % <= 0.0500 %
Other, total  <= 0.400 % <= 0.400 %
Oxygen, O  <= 0.200 % <= 0.200 %
Titanium, Ti  96.06 - 98.0 % 96.06 - 98.0 % As Balance; Elemental Compostions per ASTM B265

Users viewing this material also viewed the following:
Titanium Ti-6Al-2Sn-4Zr-2Mo-0.1Si; Duplex Annealed
Titanium Ti-3Al-2.5V (Grade 9), alpha annealed
Titanium IMI 230 (Ti-2.5Cu), aged
Titanium Ti-5Al-2.5Sn (Grade 6)
Titanium 11 (Ti-6Al-2Sn-1.5Zr-1Mo-0.35Bi-0.1Si)

MTA231 / 14121
 




Machining performance

Download Ti-2.5Cu the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.