Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi5Al2.5Fe plate,Ti5Al2.5Fe Round Bar,Ti5Al2.5Fe forgings,Ti5Al2.5Fe suppliers, Ti5Al2.5Fe Stock,Ti5Al2.5Fe sheet, Ti5Al2.5Fe flat bar, Ti5Al2.5Fe pipe,Ti5Al2.5Fe tube,Ti5Al2.5Fe mould,Ti5Al2.5Fe round ingot,Ti5Al2.5Fe cold-rolled steel,Ti5Al2.5Fe coil,Ti5Al2.5Fe strap steel,Ti5Al2.5Fe hot-rolled steel,Ti5Al2.5Fe medium plate, Ti5Al2.5Fe heavy plate,Ti5Al2.5Fe shapped bar,Ti5Al2.5Fe hexahedral bar,Ti5Al2.5Fe,Ti5Al2.5Fe slab ingot,Ti5Al2.5Fe slab,Ti5Al2.5Fe price,Ti5Al2.5Fe square bar,Ti5Al2.5Fe square steel,Ti5Al2.5Fe wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti5Al2.5Fe.

Current Location:Home » Products » Ti Alloy » Ti5Al2.5Fe

Product category

Ti5Al2.5Fe

Data Table for:Products: Ti Alloy:Ti5Al2.5Fe

Ti5Al2.5Fe properties and heat treatment forged piece, Including Ti5Al2.5Fe application and specifications, We have all specifications,Including Ti5Al2.5Fe steel plate, Ti5Al2.5Fe sheet, Ti5Al2.5Fe square steel, Ti5Al2.5Fe flat bar,Ti5Al2.5Fe round bar,Ti5Al2.5Fe forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti5Al2.5Fe has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti5Al2.5Fe and Standards

Ti5Al2.5Fe ISO 5832/X
Categories: Metal; Nonferrous Metal; Titanium Alloy; Alpha/Beta Titanium Alloy
Key Words: medical, surgical

Physical Properties Metric English Comments
Density  4.45 g/cc 0.161 lb/in³
 
Mechanical Properties Metric English Comments
Modulus of Elasticity  110 - 116 GPa 16000 - 16800 ksi
 
Thermal Properties Metric English Comments
CTE, linear  9.30 µm/m-°C
@Temperature 30.0 - 200 °C
5.17 µin/in-°F
@Temperature 86.0 - 392 °F
Transformation Temperature  935 - 965 °C 1720 - 1770 °F
 
Component Elements Properties Metric English Comments
Aluminum, Al  4.50 - 5.50 % 4.50 - 5.50 %
Carbon, C  0.080 % 0.080 %
Hydrogen, H  0.015 % 0.015 %
Iron, Fe  2.0 - 3.0 % 2.0 - 3.0 %
Nitrogen, N  0.050 % 0.050 %
Other, each  0.10 % 0.10 %
Other, total  0.40 % 0.40 %
Oxygen, O  0.20 % 0.20 %
Titanium, Ti  90.755 - 92.755 % 90.755 - 92.755 %
 
Descriptive Properties
Microstructure Al-A9
Phase at room temp a+ß

Users viewing this material also viewed the following:
Ti6Al7Nb ASTM F1295
Overview of materials for Alpha/Beta Titanium Alloy
Overview of materials for 7000 Series Aluminum Alloy
Titanium, Ti
Ti15Mo5Zr3Al ß titanium alloy

MMEDIC24 / 12400
 




Machining performance

Download Ti5Al2.5Fe the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:Ti5Al2.5Fe steel plate, Ti5Al2.5Fe sheet, Ti5Al2.5Fe square steel, Ti5Al2.5Fe flat bar,Ti5Al2.5Fe round bar,Ti5Al2.5Fe forgings