Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi30Ta plate,Ti30Ta Round Bar,Ti30Ta forgings,Ti30Ta suppliers, Ti30Ta Stock,Ti30Ta sheet, Ti30Ta flat bar, Ti30Ta pipe,Ti30Ta tube,Ti30Ta mould,Ti30Ta round ingot,Ti30Ta cold-rolled steel,Ti30Ta coil,Ti30Ta strap steel,Ti30Ta hot-rolled steel,Ti30Ta medium plate, Ti30Ta heavy plate,Ti30Ta shapped bar,Ti30Ta hexahedral bar,Ti30Ta,Ti30Ta slab ingot,Ti30Ta slab,Ti30Ta price,Ti30Ta square bar,Ti30Ta square steel,Ti30Ta wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti30Ta.

Current Location:Home » Products » Ti Alloy » Ti30Ta

Product category

Ti30Ta

Data Table for:Products: Ti Alloy:Ti30Ta

Ti30Ta properties and heat treatment forged piece, Including Ti30Ta application and specifications, We have all specifications,Including Ti30Ta steel plate, Ti30Ta sheet, Ti30Ta square steel, Ti30Ta flat bar,Ti30Ta round bar,Ti30Ta forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Ti30Ta has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Ti30Ta and Standards

Ti30Ta ß titanium alloy
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Key Words: medical, surgical

Mechanical Properties Metric English Comments
Tensile Strength, Ultimate  740 MPa 107000 psi as rolled
  800 MPa 116000 psi annealed at 1100°C
  800 MPa 116000 psi annealed at 1400°C
Tensile Strength, Yield  590 MPa 85600 psi as rolled
  650 MPa 94300 psi 0.2%, annealed at 1100°C
  680 MPa 98600 psi 0.2%, annealed at 1400°C
Elongation at Break  6.00 % 6.00 % annealed at 1400°C
  8.00 % 8.00 % annealed at 1100°C
  28.0 % 28.0 % as rolled
Reduction of Area  18.0 % 18.0 % annealed at 1400°C
  42.0 % 42.0 % annealed at 1100°C
  58.0 % 58.0 % as rolled
Modulus of Elasticity  63.0 GPa 9140 ksi 1h / 1000°C / water
  80.0 GPa 11600 ksi As rolled
 
Component Elements Properties Metric English Comments
Tantalum, Ta  30.0 % 30.0 %
Titanium, Ti  70.0 % 70.0 %

Users viewing this material also viewed the following:
Ti30Nb ß titanium alloy
Ti15Mo5Zr3Al ß titanium alloy
Overview of materials for Beta Titanium Alloy
Titanium Alloys, General
Ti12Mo5Zr5Sn ß titanium alloy

MMEDIC29 / 12405
 




Machining performance

Download Ti30Ta the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.