Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelTP304L plate,TP304L Round Bar,TP304L forgings,TP304L suppliers, TP304L Stock,TP304L sheet, TP304L flat bar, TP304L pipe,TP304L tube,TP304L mould,TP304L round ingot,TP304L cold-rolled steel,TP304L coil,TP304L strap steel,TP304L hot-rolled steel,TP304L medium plate, TP304L heavy plate,TP304L shapped bar,TP304L hexahedral bar,TP304L,TP304L slab ingot,TP304L slab,TP304L price,TP304L square bar,TP304L square steel,TP304L wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of TP304L.

Current Location:Home » Products » Stainless Steel » TP304L

Product category

TP304L

Data Table for:Products: Stainless Steel:TP304L

TP304L properties and heat treatment forged piece, Including TP304L application and specifications, We have all specifications,Including TP304L steel plate, TP304L sheet, TP304L square steel, TP304L flat bar,TP304L round bar,TP304L forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the TP304L has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade TP304L and Standards

Production acc. to the standard of GB / ASTM / ASME / DIN / JIS etc.
Types:
Elbows, seamless and welded, LR & SR
Equal and reducing Tees, seamless and welded
Concentric and eccentric Reducers
Lap-joint stub ends, seamless and welded
Caps, Seamless and welded
Special Fitting, made out of plate or solid bar material acc. to specifications
Wall thickness: From Sch5 to Sch160
Material Grades:
0Cr18Ni9, 0Cr18Ni9Ti, 1Cr18Ni9Ti, 0Cr18Ni12Mo2Ti,00Cr18Ni10, 00Cr19Ni11, 00Cr17Ni13Mo2,TP304,TP304L,TP316,TP316L,TP321
Dimensions:
Seamless: from 1/2’ up to 28’
Welded: from 1/2’ up to 58’
Treatment and packing and blasting and marking:
To all requirement acc. to customer’s specification




Machining performance

Download TP304L the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:TP304L steel plate, TP304L sheet, TP304L square steel, TP304L flat bar,TP304L round bar,TP304L forgings