Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelSAE 945X plate,SAE 945X Round Bar,SAE 945X forgings,SAE 945X suppliers, SAE 945X Stock,SAE 945X sheet, SAE 945X flat bar, SAE 945X pipe,SAE 945X tube,SAE 945X mould,SAE 945X round ingot,SAE 945X cold-rolled steel,SAE 945X coil,SAE 945X strap steel,SAE 945X hot-rolled steel,SAE 945X medium plate, SAE 945X heavy plate,SAE 945X shapped bar,SAE 945X hexahedral bar,SAE 945X,SAE 945X slab ingot,SAE 945X slab,SAE 945X price,SAE 945X square bar,SAE 945X square steel,SAE 945X wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of SAE 945X.

Current Location:Home » Products » Alloy steel » SAE 945X

Product category

SAE 945X

Data Table for:Products: Alloy steel:SAE 945X

SAE 945X properties and heat treatment forged piece, Including SAE 945X application and specifications, We have all specifications,Including SAE 945X steel plate, SAE 945X sheet, SAE 945X square steel, SAE 945X flat bar,SAE 945X round bar,SAE 945X forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the SAE 945X has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade SAE 945X and Standards

High-Strength Low-Alloy steel
SAE 945X HSLA steel
Chemical Composition
Element
Weight %
C
 0.22 
Mn
 1.35 
P
 0.04 
S
 0.05 
Si
 0.90 
Mechanical Properties
Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 
Tensile Strength (Mpa)
415 
25 
(sheet and strip)
Yield Strength (Mpa)
310 
Elongation (%)
25 
Reduction in Area (%)



Machining performance

Download SAE 945X the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.