Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelS460QL1 plate,S460QL1 Round Bar,S460QL1 forgings,S460QL1 suppliers, S460QL1 Stock,S460QL1 sheet, S460QL1 flat bar, S460QL1 pipe,S460QL1 tube,S460QL1 mould,S460QL1 round ingot,S460QL1 cold-rolled steel,S460QL1 coil,S460QL1 strap steel,S460QL1 hot-rolled steel,S460QL1 medium plate, S460QL1 heavy plate,S460QL1 shapped bar,S460QL1 hexahedral bar,S460QL1,S460QL1 slab ingot,S460QL1 slab,S460QL1 price,S460QL1 square bar,S460QL1 square steel,S460QL1 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of S460QL1.

Current Location:Home » Products » Alloy steel » S460QL1

Product category

S460QL1

Data Table for:Products: Alloy steel:S460QL1

S460QL1 properties and heat treatment forged piece, Including S460QL1 application and specifications, We have all specifications,Including S460QL1 steel plate, S460QL1 sheet, S460QL1 square steel, S460QL1 flat bar,S460QL1 round bar,S460QL1 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the S460QL1 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade S460QL1 and Standards

S460QL1   ( 1.8916 )
    Grade :     S460QL1
    Number:     1.8916
    Standard: EN 10025 - 6 : 2004   Technical delivery conditions for flat products of high yield strength structural steels in the quenched and tempered condition
    Classification:     High yield strength structural steels in the quenched and tempered condition

 

Chemical composition % of the ladle analysis   of grade   S460QL1 (1.8916)

Nominal thickness =< 50(mm) CEV max = 0.47
Nominal thickness from 50 to 100 (mm) CEV max = 0.48
Depending on the thickness of the product and the manufacturing conditions, the manufacturer may add to the steel one or several alloying elements up to the maximum values given in order to obtain the specified properties
Nb, Ti, V, Zr: There shall be at least 0.015% of a grain-refining element present. AL is also one of these elements. The minimum content of 0.015% applies to soluble aluminium, this value is regarded as attained if the total aluminium content is at least 0.018%; in case of dispute the soluble aluminium content shall be determined
 

C Si Mn Ni P S Cr Mo V N Nb Ti Cu Zr B CEV
max   0.2 max   0.8 max   1.7 max   2 max   0.02 max   0.01 max   1.5 max   0.7 max   0.12 max   0.015 max   0.06 max   0.05 max   0.5 max   0.15 max   0.005 max   0.5

 

Mechanical properties of grade   S460QL1 (1.8916)


Temperature -60 -40 -20 0
Notch impact test. Min. absorbed energy 30 40 50 60

Nominal thickness (mm) 3 - 50 50 - 100 100 - 150
ReH - Minimum yield strength (MPa) 460 440 400

Nominal thickness (mm) 3 - 50 50 - 100 100 - 150
Rm -Tensile strength (MPa) 550-720 550-720 500-670
.
Nominal thickness (mm) -
A - Minimum elongation Lo = 5,65 √ So (%) 17



Equivalent grades of grade   S460QL1 (1.8916)

Germany
DIN,WNr
France
AFNOR
TStE460V
E460T




Machining performance

Download S460QL1 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.