Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelInconel 625 plate,Inconel 625 Round Bar,Inconel 625 forgings,Inconel 625 suppliers, Inconel 625 Stock,Inconel 625 sheet, Inconel 625 flat bar, Inconel 625 pipe,Inconel 625 tube,Inconel 625 mould,Inconel 625 round ingot,Inconel 625 cold-rolled steel,Inconel 625 coil,Inconel 625 strap steel,Inconel 625 hot-rolled steel,Inconel 625 medium plate, Inconel 625 heavy plate,Inconel 625 shapped bar,Inconel 625 hexahedral bar,Inconel 625,Inconel 625 slab ingot,Inconel 625 slab,Inconel 625 price,Inconel 625 square bar,Inconel 625 square steel,Inconel 625 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Inconel 625.

Current Location:Home » Products » Alloy steel » Inconel 625

Product category

Inconel 625

Data Table for:Products: Alloy steel:Inconel 625

Inconel 625 properties and heat treatment forged piece, Including Inconel 625 application and specifications, We have all specifications,Including Inconel 625 steel plate, Inconel 625 sheet, Inconel 625 square steel, Inconel 625 flat bar,Inconel 625 round bar,Inconel 625 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the Inconel 625 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade Inconel 625 and Standards

INCONEL® Alloy 625
UNS Number N06625
Other common names: Alloy 625
Inconel 625 is a corrosion and oxidation resistant nickel alloy that is used both for its high strength and outstanding aqueous corrosion resistance. Its outstanding strength and toughness is due to the addition of niobium which acts with the molybdenum to stiffen the alloy’s matrix. Alloy 625 has excellent fatigue strength and stress-corrosion cracking resistance to chloride ions. This nickel alloy has excellent weldability and is frequently used to weld AL-6XN. This alloy resists a wide range of severely corrosive environments and is especially resistant to pitting and crevice corrosion. Some typical applications Inconel 625 is used in are chemical processing, aerospace and marine engineering, pollution-control equipment, and nuclear reactors.
In what form is Inconel 625 available at Mega Mex?
What are the characteristics of Inconel 625?
Chemical Composition, %

Cr Ni Mo Co + Nb Ta Al Ti C
20.00-30.00 Remainder 8.0-10.0 1.0 max 3.15-4.15 .40 max .40 max .10 max
Fe Mn Si P S      
5.0 max .50 max .50 max .015 max .015 max      

In what applications is Inconel 625 used?
Fabrication with Inconel 625
Alloy 625 has excellent forming and welding characteristics. It may be forged or hot worked providing temperature is maintained in the range of about 1800-2150° F. Ideally, to control grain size, finish hot working operations should be performed at the lower end of the temperature range. Because of its good ductility, alloy 625 is also readily formed by cold working. However, the alloy does work-harden rapidly so intermediate annealing treatments may be needed for complex component forming operations. In order to restore the best balance of properties, all hot or cold worked parts should be annealed and rapidly cooled. This nickel alloy can be welded by both manual and automatic welding methods, including gas tungsten arc, gas metal arc, electron beam and resistance welding. It exhibits good restraint welding characteristics.
For more information on fabrication and machining, click here.
ASTM Specifications

Pipe Smls Pipe Welded Tube Smls Tube Welded Sheet/Plate Bar Forging Fitting Wire
B444 B705 B444 B704 B443 B446 - - -

Mechanical Properties
Representative Tensile Properties, bar, 1800° F anneal

Temp° F Tensile (psi) .2% Yield (psi) Elongation in 2 “ (%)
70 144,000 84,000 44
400 134,000 66,000 45
600 132,000 63,000 42.5
800 131,500 61,000 45
1000 130,000 60,500 48
1200 119,000 60,000 34
1400 78,000 58,500 59
1600 40,000 39,000 117




Machining performance

Download Inconel 625 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.