Our to produce better steel-based products are the main used in industrial manufacturing various types Stainless SteelE295 plate,E295 Round Bar,E295 forgings,E295 suppliers, E295 Stock,E295 sheet, E295 flat bar, E295 pipe,E295 tube,E295 mould,E295 round ingot,E295 cold-rolled steel,E295 coil,E295 strap steel,E295 hot-rolled steel,E295 medium plate, E295 heavy plate,E295 shapped bar,E295 hexahedral bar,E295,E295 slab ingot,E295 slab,E295 price,E295 square bar,E295 square steel,E295 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of E295.

Current Location:Home » Products » Stainless Steel » E295

Product category

E295

Data Table for:Products: Stainless Steel:E295

E295 properties and heat treatment forged piece, Including E295 application and specifications, We have all specifications,Including E295 steel plate, E295 sheet, E295 square steel, E295 flat bar,E295 round bar,E295 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the E295 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade E295 and Standards

 

E295   ( 1.0050 )
    Grade :     E295
    Number:     1.0050
    Standard: EN 10025 - 2 : 2004   Technical delivery conditions for non-alloy structural steels
    Classification:     Non-alloy structural steels
    Equivalent grades:     Go here

 

Chemical composition % of the ladle analysis   of grade   E295 (1.0050)
P S N
max   0.045 max   0.045 max   0.012

 

Mechanical properties of grade   E295 (1.0050)


Nominal thickness (mm) to 16 16 - 40 40 - 63 63 - 80 80 - 100 100 - 125
ReH - Minimum yield strength (MPa) 295 285 275 265 255 245

Nominal thickness (mm) 3 - 100 100 - 125
Rm -Tensile strength (MPa) 470-610 450-610
.
Nominal thickness (mm) 3 - 40 40 - 63 63 - 100 100 - 125
A - Minimum elongation Lo = 5,65 √ So (%) 20 19 18 16

Equivalent grades of grade   E295 (1.0050)

Germany
DIN,WNr
France
AFNOR
European old
EN
Italy
UNI
Spain
UNE
China
GB
Sweden
SS
Austria
ONORM
Russia
GOST
St50-2
A50-2
Fe490-2
Fe490
A490-2
Q275Z
1550-00
1550-01
St490
S285
St5ps
St5sp




Machining performance

Download E295 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:E295 steel plate, E295 sheet, E295 square steel, E295 flat bar,E295 round bar,E295 forgings