Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelDIN 1.2379 plate,DIN 1.2379 Round Bar,DIN 1.2379 forgings,DIN 1.2379 suppliers, DIN 1.2379 Stock,DIN 1.2379 sheet, DIN 1.2379 flat bar, DIN 1.2379 pipe,DIN 1.2379 tube,DIN 1.2379 mould,DIN 1.2379 round ingot,DIN 1.2379 cold-rolled steel,DIN 1.2379 coil,DIN 1.2379 strap steel,DIN 1.2379 hot-rolled steel,DIN 1.2379 medium plate, DIN 1.2379 heavy plate,DIN 1.2379 shapped bar,DIN 1.2379 hexahedral bar,DIN 1.2379,DIN 1.2379 slab ingot,DIN 1.2379 slab,DIN 1.2379 price,DIN 1.2379 square bar,DIN 1.2379 square steel,DIN 1.2379 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of DIN 1.2379.

Current Location:Home » Products » Tool steel » DIN 1.2379

Product category

DIN 1.2379

Data Table for:Products: Tool steel:DIN 1.2379

DIN 1.2379 properties and heat treatment forged piece, Including DIN 1.2379 application and specifications, We have all specifications,Including DIN 1.2379 steel plate, DIN 1.2379 sheet, DIN 1.2379 square steel, DIN 1.2379 flat bar,DIN 1.2379 round bar,DIN 1.2379 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the DIN 1.2379 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade DIN 1.2379 and Standards

Category  steel
Class  Tool steel
Type  High-carbon, high-chromium cold work steel
Designations  Germany: DIN 1.2379
Italy: UNI KU
United Kingdom: B.S. BD 2
United States: ASTM A681 , FED QQ-T-570 , SAE J437 , SAE J438 , UNS T30402

Composition
Element Weight %
C  1.40-1.60 
Mn  0.60 
Si  0.60 
Cr  11.00-13.00 
Ni  0.30 
Mo  0.70-1.20 
V  1.10 
Co  1.00 
Cu  0.25 
P  0.03 
S  0.03 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  

Thermal Properties
Properties  Conditions 
T (°C) Treatment
Thermal Expansion (10-6/ºC) 10.4  20-100 more  




Machining performance

Download DIN 1.2379 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.