Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelASTM A621 plate,ASTM A621 Round Bar,ASTM A621 forgings,ASTM A621 suppliers, ASTM A621 Stock,ASTM A621 sheet, ASTM A621 flat bar, ASTM A621 pipe,ASTM A621 tube,ASTM A621 mould,ASTM A621 round ingot,ASTM A621 cold-rolled steel,ASTM A621 coil,ASTM A621 strap steel,ASTM A621 hot-rolled steel,ASTM A621 medium plate, ASTM A621 heavy plate,ASTM A621 shapped bar,ASTM A621 hexahedral bar,ASTM A621,ASTM A621 slab ingot,ASTM A621 slab,ASTM A621 price,ASTM A621 square bar,ASTM A621 square steel,ASTM A621 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A621.

Current Location:Home » Products » Carbon steel » ASTM A621

Product category

ASTM A621

Data Table for:Products: Carbon steel:ASTM A621

ASTM A621 properties and heat treatment forged piece, Including ASTM A621 application and specifications, We have all specifications,Including ASTM A621 steel plate, ASTM A621 sheet, ASTM A621 square steel, ASTM A621 flat bar,ASTM A621 round bar,ASTM A621 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM A621 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM A621 and Standards

Category  steel
Class  Carbon steel

Composition
Element Weight %
C  0.10 
Mn  0.50 
P  0.025 
S  0.04 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  




Machining performance

Download ASTM A621 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM A621 steel plate, ASTM A621 sheet, ASTM A621 square steel, ASTM A621 flat bar,ASTM A621 round bar,ASTM A621 forgings