Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelASTM A611 Grade C plate,ASTM A611 Grade C Round Bar,ASTM A611 Grade C forgings,ASTM A611 Grade C suppliers, ASTM A611 Grade C Stock,ASTM A611 Grade C sheet, ASTM A611 Grade C flat bar, ASTM A611 Grade C pipe,ASTM A611 Grade C tube,ASTM A611 Grade C mould,ASTM A611 Grade C round ingot,ASTM A611 Grade C cold-rolled steel,ASTM A611 Grade C coil,ASTM A611 Grade C strap steel,ASTM A611 Grade C hot-rolled steel,ASTM A611 Grade C medium plate, ASTM A611 Grade C heavy plate,ASTM A611 Grade C shapped bar,ASTM A611 Grade C hexahedral bar,ASTM A611 Grade C,ASTM A611 Grade C slab ingot,ASTM A611 Grade C slab,ASTM A611 Grade C price,ASTM A611 Grade C square bar,ASTM A611 Grade C square steel,ASTM A611 Grade C wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A611 Grade C.

Current Location:Home » Products » Carbon steel » ASTM A611 Grade C

Product category

ASTM A611 Grade C

Data Table for:Products: Carbon steel:ASTM A611 Grade C

ASTM A611 Grade C properties and heat treatment forged piece, Including ASTM A611 Grade C application and specifications, We have all specifications,Including ASTM A611 Grade C steel plate, ASTM A611 Grade C sheet, ASTM A611 Grade C square steel, ASTM A611 Grade C flat bar,ASTM A611 Grade C round bar,ASTM A611 Grade C forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM A611 Grade C has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM A611 Grade C and Standards

 

Category  steel
Class  Carbon steel

Composition
Element Weight %
C  0.20 
Mn  0.60 
P  0.04 
S  0.04 
Cu  0.20 (min) 
Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 330  25   
Yield Strength (Mpa) 230 
Elongation (%) 22 
Reduction in Area (%)  



Machining performance

Download ASTM A611 Grade C the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.