Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelASTM A573 Grade 65 plate,ASTM A573 Grade 65 Round Bar,ASTM A573 Grade 65 forgings,ASTM A573 Grade 65 suppliers, ASTM A573 Grade 65 Stock,ASTM A573 Grade 65 sheet, ASTM A573 Grade 65 flat bar, ASTM A573 Grade 65 pipe,ASTM A573 Grade 65 tube,ASTM A573 Grade 65 mould,ASTM A573 Grade 65 round ingot,ASTM A573 Grade 65 cold-rolled steel,ASTM A573 Grade 65 coil,ASTM A573 Grade 65 strap steel,ASTM A573 Grade 65 hot-rolled steel,ASTM A573 Grade 65 medium plate, ASTM A573 Grade 65 heavy plate,ASTM A573 Grade 65 shapped bar,ASTM A573 Grade 65 hexahedral bar,ASTM A573 Grade 65,ASTM A573 Grade 65 slab ingot,ASTM A573 Grade 65 slab,ASTM A573 Grade 65 price,ASTM A573 Grade 65 square bar,ASTM A573 Grade 65 square steel,ASTM A573 Grade 65 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A573 Grade 65.

Current Location:Home » Products » Carbon steel » ASTM A573 Grade 65

Product category

ASTM A573 Grade 65

Data Table for:Products: Carbon steel:ASTM A573 Grade 65

ASTM A573 Grade 65 properties and heat treatment forged piece, Including ASTM A573 Grade 65 application and specifications, We have all specifications,Including ASTM A573 Grade 65 steel plate, ASTM A573 Grade 65 sheet, ASTM A573 Grade 65 square steel, ASTM A573 Grade 65 flat bar,ASTM A573 Grade 65 round bar,ASTM A573 Grade 65 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM A573 Grade 65 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM A573 Grade 65 and Standards

Category  steel
Class  Carbon steel
Designations  United States: UNS K02404

Composition
Element Weight %
C  0.26 
Mn  0.85-1.20 
P  0.04 (max) 
S  0.05 (max) 
Si  0.15-0.30 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 450-530 25   




Machining performance

Download ASTM A573 Grade 65 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.