Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelASTM A570 Grade 50 plate,ASTM A570 Grade 50 Round Bar,ASTM A570 Grade 50 forgings,ASTM A570 Grade 50 suppliers, ASTM A570 Grade 50 Stock,ASTM A570 Grade 50 sheet, ASTM A570 Grade 50 flat bar, ASTM A570 Grade 50 pipe,ASTM A570 Grade 50 tube,ASTM A570 Grade 50 mould,ASTM A570 Grade 50 round ingot,ASTM A570 Grade 50 cold-rolled steel,ASTM A570 Grade 50 coil,ASTM A570 Grade 50 strap steel,ASTM A570 Grade 50 hot-rolled steel,ASTM A570 Grade 50 medium plate, ASTM A570 Grade 50 heavy plate,ASTM A570 Grade 50 shapped bar,ASTM A570 Grade 50 hexahedral bar,ASTM A570 Grade 50,ASTM A570 Grade 50 slab ingot,ASTM A570 Grade 50 slab,ASTM A570 Grade 50 price,ASTM A570 Grade 50 square bar,ASTM A570 Grade 50 square steel,ASTM A570 Grade 50 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A570 Grade 50.

Current Location:Home » Products » Carbon steel » ASTM A570 Grade 50

Product category

ASTM A570 Grade 50

Data Table for:Products: Carbon steel:ASTM A570 Grade 50

ASTM A570 Grade 50 properties and heat treatment forged piece, Including ASTM A570 Grade 50 application and specifications, We have all specifications,Including ASTM A570 Grade 50 steel plate, ASTM A570 Grade 50 sheet, ASTM A570 Grade 50 square steel, ASTM A570 Grade 50 flat bar,ASTM A570 Grade 50 round bar,ASTM A570 Grade 50 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM A570 Grade 50 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM A570 Grade 50 and Standards

Category  steel
Class  Carbon steel

Composition
Element Weight %
C  0.25 
Mn  1.35 
P  0.04 
S  0.05 
Cu  0.20 (min) 

Mechanical Properties
Properties  Conditions 
T (°C) Treatment
Density (×1000 kg/m3) 7.7-8.03 25  
Poisson's Ratio 0.27-0.30 25  
Elastic Modulus (GPa) 190-210 25  
Tensile Strength (Mpa) 450  25   




Machining performance

Download ASTM A570 Grade 50 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.





Hot tags:ASTM A570 Grade 50 steel plate, ASTM A570 Grade 50 sheet, ASTM A570 Grade 50 square steel, ASTM A570 Grade 50 flat bar,ASTM A570 Grade 50 round bar,ASTM A570 Grade 50 forgings