Our to produce better steel-based products are the main used in industrial manufacturing various types Carbon steelASTM A529 Grade 50 plate,ASTM A529 Grade 50 Round Bar,ASTM A529 Grade 50 forgings,ASTM A529 Grade 50 suppliers, ASTM A529 Grade 50 Stock,ASTM A529 Grade 50 sheet, ASTM A529 Grade 50 flat bar, ASTM A529 Grade 50 pipe,ASTM A529 Grade 50 tube,ASTM A529 Grade 50 mould,ASTM A529 Grade 50 round ingot,ASTM A529 Grade 50 cold-rolled steel,ASTM A529 Grade 50 coil,ASTM A529 Grade 50 strap steel,ASTM A529 Grade 50 hot-rolled steel,ASTM A529 Grade 50 medium plate, ASTM A529 Grade 50 heavy plate,ASTM A529 Grade 50 shapped bar,ASTM A529 Grade 50 hexahedral bar,ASTM A529 Grade 50,ASTM A529 Grade 50 slab ingot,ASTM A529 Grade 50 slab,ASTM A529 Grade 50 price,ASTM A529 Grade 50 square bar,ASTM A529 Grade 50 square steel,ASTM A529 Grade 50 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of ASTM A529 Grade 50.

Current Location:Home » Products » Carbon steel » ASTM A529 Grade 50

Product category

ASTM A529 Grade 50

Data Table for:Products: Carbon steel:ASTM A529 Grade 50

ASTM A529 Grade 50 properties and heat treatment forged piece, Including ASTM A529 Grade 50 application and specifications, We have all specifications,Including ASTM A529 Grade 50 steel plate, ASTM A529 Grade 50 sheet, ASTM A529 Grade 50 square steel, ASTM A529 Grade 50 flat bar,ASTM A529 Grade 50 round bar,ASTM A529 Grade 50 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the ASTM A529 Grade 50 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade ASTM A529 Grade 50 and Standards

ASTM A529 Grade 50 3/16 to 1 in. thick, as-rolled steel plate

Categories: Metal; Ferrous Metal; ASTM Steel; Carbon Steel; Low Carbon steel

Material Notes: A low cost grade limited to 1/2 inch thickness, used occasionally for non-demanding applications.
The following are suggested consumables for arc welding processes for 0.476 - 1.27 cm (3/16 - 1/2 in.) thicknesses. For Manual Shielded Metal-Arc (AWS A5.5) use Low Hydrogen Electrodes E60xx, and E70xx. For Submerged Arc (AWS A5.23) use F6x-Exxx, and F7x-Exxx. For Gas Metal-Arc (AWS A5.28) use ER70S-x. For Flux Cored-Arc (AWS A5.29) use E6xT-x, and E7xT-x except -2, -3, -10, or -GS.


Physical Properties Metric English Comments
Density  7.85 g/cc 0.284 lb/in³ Typical of ASTM steel
 
Mechanical Properties Metric English Comments
Tensile Strength at Break  483 - 689 MPa 70000 - 100000 psi
Tensile Strength, Yield  >= 345 MPa >= 50000 psi
Elongation at Break  >= 16.0 % >= 16.0 % in 8"
  >= 19.0 % >= 19.0 % in 2"
 
Component Elements Properties Metric English Comments
Carbon, C  <= 0.270 % <= 0.270 %
Copper, Cu  >= 0.20 % >= 0.20 %
Iron, Fe  >= 97.69 % >= 97.69 %
Manganese, Mn  <= 1.35 % <= 1.35 %
Phosphorous, P  <= 0.040 % <= 0.040 %
Silicon, Si  <= 0.40 % <= 0.40 %
Sulfur, S  <= 0.050 % <= 0.050 %

 




Machining performance

Download ASTM A529 Grade 50 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.