Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelAISI P3 plate,AISI P3 Round Bar,AISI P3 forgings,AISI P3 suppliers, AISI P3 Stock,AISI P3 sheet, AISI P3 flat bar, AISI P3 pipe,AISI P3 tube,AISI P3 mould,AISI P3 round ingot,AISI P3 cold-rolled steel,AISI P3 coil,AISI P3 strap steel,AISI P3 hot-rolled steel,AISI P3 medium plate, AISI P3 heavy plate,AISI P3 shapped bar,AISI P3 hexahedral bar,AISI P3,AISI P3 slab ingot,AISI P3 slab,AISI P3 price,AISI P3 square bar,AISI P3 square steel,AISI P3 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI P3.

Current Location:Home » Products » Tool steel » AISI P3

Product category

AISI P3

Data Table for:Products: Tool steel:AISI P3

AISI P3 properties and heat treatment forged piece, Including AISI P3 application and specifications, We have all specifications,Including AISI P3 steel plate, AISI P3 sheet, AISI P3 square steel, AISI P3 flat bar,AISI P3 round bar,AISI P3 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI P3 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI P3 and Standards

Designations 
United States: ASTM A681 , UNS T51603

Chemical Composition
Element
Weight %
C
 0.10 
Mn
 0.20-0.60 
Si
 0.40 
Cr
 0.40-0.75 
Ni
 1.00-1.50 
Cu
 0.25 
P
 0.03 
S
 0.03 
 
Mechanical Properties
Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 



Machining performance

Download AISI P3 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.