Our to produce better steel-based products are the main used in industrial manufacturing various types Tool steelAISI H23 plate,AISI H23 Round Bar,AISI H23 forgings,AISI H23 suppliers, AISI H23 Stock,AISI H23 sheet, AISI H23 flat bar, AISI H23 pipe,AISI H23 tube,AISI H23 mould,AISI H23 round ingot,AISI H23 cold-rolled steel,AISI H23 coil,AISI H23 strap steel,AISI H23 hot-rolled steel,AISI H23 medium plate, AISI H23 heavy plate,AISI H23 shapped bar,AISI H23 hexahedral bar,AISI H23,AISI H23 slab ingot,AISI H23 slab,AISI H23 price,AISI H23 square bar,AISI H23 square steel,AISI H23 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI H23.

Current Location:Home » Products » Tool steel » AISI H23

Product category

AISI H23

Data Table for:Products: Tool steel:AISI H23

AISI H23 properties and heat treatment forged piece, Including AISI H23 application and specifications, We have all specifications,Including AISI H23 steel plate, AISI H23 sheet, AISI H23 square steel, AISI H23 flat bar,AISI H23 round bar,AISI H23 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI H23 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI H23 and Standards

Designations
Germany: DIN 1.2625
United States: ASTM A681 , FED QQ-T-570 , UNS T20823

 
Chemical Composition:

Element
Weight %
C
 0.25-0.35 
Mn
 0.15-0.40 
Si
 0.15-0.60 
Cr
 11.00-12.75 
Ni
 0.3 
W
 11.00-12.75 
V
 0.75-1.25 
Cu
 0.25 
P
 0.03 
S
 0.03 

Mechanical Properties:

Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 




Machining performance

Download AISI H23 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.