Our to produce better steel-based products are the main used in industrial manufacturing various types Alloy steelAISI 52100 plate,AISI 52100 Round Bar,AISI 52100 forgings,AISI 52100 suppliers, AISI 52100 Stock,AISI 52100 sheet, AISI 52100 flat bar, AISI 52100 pipe,AISI 52100 tube,AISI 52100 mould,AISI 52100 round ingot,AISI 52100 cold-rolled steel,AISI 52100 coil,AISI 52100 strap steel,AISI 52100 hot-rolled steel,AISI 52100 medium plate, AISI 52100 heavy plate,AISI 52100 shapped bar,AISI 52100 hexahedral bar,AISI 52100,AISI 52100 slab ingot,AISI 52100 slab,AISI 52100 price,AISI 52100 square bar,AISI 52100 square steel,AISI 52100 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of AISI 52100.

Current Location:Home » Products » Alloy steel » AISI 52100

Product category

AISI 52100

Data Table for:Products: Alloy steel:AISI 52100

AISI 52100 properties and heat treatment forged piece, Including AISI 52100 application and specifications, We have all specifications,Including AISI 52100 steel plate, AISI 52100 sheet, AISI 52100 square steel, AISI 52100 flat bar,AISI 52100 round bar,AISI 52100 forgings, we can own production and sales.


Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel


We can produce the AISI 52100 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.


Chemical composition % of the ladle analysis of grade AISI 52100 and Standards

Alloy Steel

AISI 52100 Alloy Steel

 

Designations 
United States: UNS G52986

 

Chemical Composition

 

Element
Weight %
C
 0.98-1.10 
Mn
 0.25-0.45 
P
 0.025 (max) 
S
 0.025 (max) 
Si
 0.15-0.30 
Cr
 1.30-1.60 

 

Mechanical Properties

 

Properties
 Conditions 
T (°C)
Treatment
Density (×1000 kg/m3)
7.7-8.03
25
 
Poisson's Ratio
0.27-0.30
25
 
Elastic Modulus (GPa)
190-210
25
 

 

 

Thermal Properties

 

Properties
 Conditions 
T (°C)
Treatment
Thermal Expansion (10-6/ºC)
11.9 
0-100
annealed

 




Machining performance

Download AISI 52100 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>


Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.


Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.


Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.


Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.


Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.